Effect of Acicular Ferrite on Cracking Sensibility in the Weld Metal of Q690+Q550 High Strength Steels

نویسندگان

  • Lei ZHANG
  • Yajiang LI
  • Qinglei JIANG
چکیده

High strength steels Q690+Q550 were welded using three different welding wires without preheating by gas shielded arc welding process. Microstructural characteristics of weld metals and nucleation mechanism of acicular ferrite were investigated by means of scanning electron microscope (SEM), energy dispersive spectrum (EDS) and transmission electron microscope (TEM). The straight Y-groove test and impact test were employed to assess cracking resistance and impact toughness of joints. Results indicated that the addition of Ti and Cr in the MK·G60-1 weld metal suppressed the formation of pro-eutectoid ferrite and ferrite side plate and contributed to the formation of acicular ferrite. The inclusions composed of (Ti, Mn) oxides and Mn, Cu sulfides became nucleation sites of primary acicular ferrite. Secondary acicular ferrites were nucleated on some pre-existing ferrite laths. Impact toughness and cracking resistance were enhanced with the increase of acicular ferrite in the weld metal.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Hydrogen-assisted stress corrosion cracking of high strength steel Division of Surface and Corrosion Science School of Chemical Science and Engineering Royal Institute of Technology, KTH

In this work, Slow Strain Rate Test (SSRT) testing, Light Optical Microscopy (LOM) and Scanning Electron Microscopy (SEM) were used to study the effect of microstructure, corrosive environments and cathodic polarisation on stress corrosion cracking (SCC) of two grades of high strength steels, Type A and Type B. Type A is manufactured by quench and tempered (Q&T) method. Type B, a normalize stee...

متن کامل

Effect of Weld Heat Input on Microstructure and Mechanical Properties of Dissimilar Joints of API-B and API-X42 Pipeline Steels

In this study, the effect of welding heat input on microstructure and mechanical properties of dissimilar joints of API-X42 and API-B pipeline steels was investigated. Evaluation of the microstructures showed that increasing the welding heat input decreased acicular ferrite in weld metal microstructure, while amount of Widmanstatten ferrite, polygonal ferrite and grain boundary ferrite increase...

متن کامل

The effect of heat input on the microstructure and hardness of continuous fiber laser welded high Al-content δ-TRIP steel

Recent research suggests that extraordinary combinations of strength and ductility can be achieved in the so-called TRIP steels. With the development of these steels, welding with small weld nugget size and acceptable strength are needed. For these reasons present study was carried out to investigate the effect of heat input onweld size, microstructure and the hardness of the welded metal of 0....

متن کامل

The effect of heat input on the microstructure and hardness of continuous fiber laser welded high Al-content δ-TRIP steel

Recent research suggests that extraordinary combinations of strength and ductility can be achieved in the so-called TRIP steels. With the development of these steels, welding with small weld nugget size and acceptable strength are needed. For these reasons present study was carried out to investigate the effect of heat input onweld size, microstructure and the hardness of the welded metal of 0....

متن کامل

Investigation of the effect of heat input on the properties of HSLA 100 steel weld joints produced by SMAW process

The microstructure and mechanical properties of HSLA-100 steel weld joints was investigated. Welding with three heat input of 0.820, 1.176 and 1.392 kJ / mm was performed using E12018 electrode. Microstructural studies were performed using scanning electron and optical microscopes. The mechanical properties of welded joints were evaluated by impact and microhardness tests. Microstructural studi...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010