Characterization of InSb Nanoparticles Synthesized Using Inert Gas Condensation
نویسندگان
چکیده
Nanoparticles (NPs) of indium antimonide (InSb) were synthesized using a vapor phase synthesis technique known as inert gas condensation (IGC). NPs were directly deposited, at room temperature and under high vacuum, on glass cover slides, TEM grids and (111) p-type silicon wafers. TEM studies showed a bimodal distribution in the size of the NPs with average particle size of 13.70 nm and 33.20 nm. The Raman spectra of InSb NPs exhibited a peak centered at 184.27 cm(-1), which corresponds to the longitudinal optical (LO) modes of phonon vibration in InSb. A 1:1 In-to-Sb composition ratio was confirmed by energy dispersive X-ray (EDX). X-ray diffractometer (XRD) and high-resolution transmission electron microscopy (HRTEM) studies revealed polycrystalline behavior of these NPs with lattice spacing around 0.37 and 0.23 nm corresponding to the growth directions of (111) and (220), respectively. The average crystallite size of the NPs obtained using XRD peak broadening results and the Debye-Scherrer formula was 25.62 nm, and the value of strain in NPs was found to be 0.0015. NP's band gap obtained using spectroscopy and Fourier transform infrared (FTIR) spectroscopy was around 0.43-0.52 eV at 300 K, which is a blue shift of 0.26-0.35 eV. The effects of increased particle density resulting into aggregation of NPs are also discussed in this paper.
منابع مشابه
The Co-Au interface in bimetallic nanoparticles: a high resolution STEM study.
We report the formation of Au/Co nanoparticles and their characterization by aberration (Cs) corrected scanning transmission electron microscopy (STEM). The nanoparticles were synthesized by inert gas condensation, forming initially core-shell and bimetallic crystals. However, after thermal treatment at normal atmospheric conditions, the Co nanoparticles changed their morphology into a fine lay...
متن کاملCharacteristics of Conductive Ink Using Octanethiolated Copper Nanoparticles Produced via Inert-gas Condensation
متن کامل
Synthesis of tungsten disulphide nanoparticles by the chemical vapor condensation method
Crystalline tungsten disulphide nanoparticles were successfully synthesized by the chemical vapor condensation (CVC) method. The process performed as decomposition of tungsten hexacarbonyl over sulphur vapor in inert gas flow, where WS2 nanoparticles were synthesized by direct reaction between as formed pure tungsten nanoclusters and sulphur vapor. Influence of experimental parameters on shape,...
متن کاملModification of Silica surface by Titanium sol synthesis and characterization
Hydrophobic silica titanium nanoparticles (STNPs) were successfully synthesized by the sol-gel process using liquid modification. Fourier transform infrared (FTIR) and X-ray fluorescence (XRF) studies were demonstrated the attachment of titanium on the silica surface. Titanium content enhanced the agglomeration of particles as shown in topography results. The N2 adsorption-desorption followed T...
متن کاملSynthesis, characterization, and gas sensing properties of In-doped ZnO nanopowders
Indium (1at %) doped ZnO and ZnO nanoparticles have been synthesized via sol gel method. The structural characters of the synthesized nanoparticles have been studied by X-ray diffraction pattern (XRD), scanning electron microscopy (SEM) and energy-dispersiveX-ray spectroscopy (EDX). From synthesized nanopowders a tablet was prepared by using the isostatic pressing and then sintered at ...
متن کامل