Low Temperature Selective Catalytic Reduction Using Molding Catalysts Mn-Ce/FA and Mn-Ce/FA-30%TiO2
نویسندگان
چکیده
Mn-Ce/FA (M) and Mn-Ce/FA-TiO2 (M), using fly ash (FA) with and without TiO2 as the carriers, were prepared by an integral molding technique. With the increase of TiO2 content, the rates of NO conversion and denitration of Mn-Ce/FA-TiO2 (M) increased, and the NO2 and N2O formation rates decreased. It is found that TiO2 could effectively inhibit the excessive oxidation of NO and the generation of N2O. The effects of space velocity, oxygen concentration and ammonia nitrogen ratio on three types of nitrogen oxides (NO, NO2, N2O) and denitration rates of the Mn-Ce/FA (M) and Mn-Ce/FA-30%TiO2 (M) were further investigated. In addition, it is demonstrated that Mn-Ce/FA (M) and Mn-Ce/FA-30%TiO2 (M) were more suitable to be used in the environment of low sulfur and less water.
منابع مشابه
Iron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3.
The catalysts of iron-doped Mn-Ce/TiO2 (Fe-Mn-Ce/TiO2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction (SCR) of NO with NH3. It was found that the NO conversion over Fe-Mn-Ce/TiO2 was obviously improved after iron doping compared with that over Mn-Ce/TiO2. Fe-Mn-Ce/TiO2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity. The results...
متن کاملThe CeOX and MnOX Nanocrystals Supported on TiO2–Graphene Oxide Catalysts and Their Selective Catalytic Reduction Properties at Low Temperature
A series of 9%CeOx–MnOx/TiO2–GO nanocomposites with different molar ratios of Ce/Mn were synthesized by the sol-gel and ultrasonic impregnation methods and characterized by field emission scanning electron microscope (FESEM), high resolution transmission electron microscopy (HRTEM), N2 adsorption (BET) analysis, X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy...
متن کاملPoisoning Effect of SO2 on Honeycomb Cordierite- Based Mn–Ce/Al2O3Catalysts for NO Reduction with NH3 at Low Temperature
Honeycomb cordierite-based Mn–Ce/Al2O3 catalysts were prepared by the impregnation method and used for low-temperature selective catalytic reduction (SCR) of NOx with NH3, with and without SO2 and/or H2O in a homemade fixed-bed tubular reactor. The catalyst reached nearly 80% NOx conversion at 100 ◦C in the absence of SO2. However, SO2 reduces the catalytic activity (80% to 72%) of the honeycom...
متن کاملLow-temperature SCR of NO with NH3 over USY-supported manganese oxide-based catalysts
A series of catalysts of manganese oxide, manganese–cerium and iron–manganese oxide supported on USY (ultra-stable Y zeolite) were studied for the low-temperature selective catalytic reduction (SCR) of NO with ammonia in the presence of excess oxygen. It was found that MnOx/USY have high activity and high selectivity to N2 in the temperature range 80–180 8C. The addition of iron and cerium oxid...
متن کاملLow Temperature Performance of Selective Catalytic Reduction of NO with NH3 under a Concentrated CO2 Atmosphere
Selective catalytic reduction of NOx with NH3 (NH3-SCR) has been widely investigated to reduce NOx emissions from combustion processes, which cause environmental challenges. However, most of the current work on NOx reduction has focused on using feed gas without CO2 or containing small amounts of CO2. In the future, oxy-fuel combustion will play an important role for power generation, and this ...
متن کامل