In Vitro Corrosion Study of Friction Stir Processed WE43 Magnesium Alloy in a Simulated Body Fluid
نویسندگان
چکیده
Corrosion behavior of friction stir processing (FSP) WE43 alloy in a simulated body fluid (SBF) was investigated. Micro-galvanic corrosion was the dominated corrosion behavior, and the corrosion resistance of FSP WE43 alloy was improved compared to the cast counterpart. Furthermore, due to the fine-grained and homogeneous microstructure, uniform corrosion morphology was observed on FSP WE43 alloy. According to the tensile properties of specimens with different immersion time intervals, FSP WE43 alloy shows better performance to maintain the mechanical integrity in SBF as compared to the as-cast alloy.
منابع مشابه
Corrosion behaviour of friction stir welded AZ61A magnesium alloy welds immersed in NaCl solutions
The extruded AZ61A magnesium alloy plates of 6 mm thickness were butt welded using friction stir welding (FSW) process. The corrosion behavior of the welds was evaluated by conducting immersion test in NaCl solution at different pH value, immersion time and chloride ion concentrations. An empirical relationship was established incorporating pH value, immersion time and chloride ion concentratio...
متن کاملFSP pass number and cooling effects on the microstructure and properties of AZ31
In this study, the effects of passes number and cooling during friction stir processing (FSP) on the microstructure and properties of AZ31 magnesium alloy has been investigated. The process was carried out at tool rotational speed, transverse speed and tool tilt angle of 1100 rpm, 52 mm/min, and 3°, respectively. Cooling was performed by water. The microstructure of FSPed samples was explored b...
متن کاملCorrosion Resistance Tests of Magnesium Alloy We43 after Extrusion
J. Przondziono, E. Hadasik, J.Szala, J. Wieczorek, Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland, W. Walke, Faculty of Biomedical Engineering, The Silesian University of Technology, Gliwice, Poland The purpose of the study was t o evaluate resistance to electrochemical corrosion of magnesium alloy WE43 after plastic working. Potentiodynamic...
متن کاملInvestigation of the effect of temperature on the corrosion behavior of welded joints similar of titanium alloy Ti-6Al-4V by friction stir welding method
In this study, corrosion behavior of Ti-6Al-4V titanium alloy joint by friction stir welding with a rotational speed of 375 rpm and a travel speed of 100 mm/min was investigated. The welding procedure was carried out under β-transus temperature that was consisted of equiaxed grains in the stir zone. The corrosion behavior of the welded joint was investigated in 3.5% NaCl solution at temperature...
متن کاملInvestigation of the effect of temperature on the corrosion behavior of welded joints similar of titanium alloy Ti-6Al-4V by friction stir welding method
In this study, corrosion behavior of Ti-6Al-4V titanium alloy joint by friction stir welding with a rotational speed of 375 rpm and a travel speed of 100 mm/min was investigated. The welding procedure was carried out under β-transus temperature that was consisted of equiaxed grains in the stir zone. The corrosion behavior of the welded joint was investigated in 3.5% NaCl solution at temperature...
متن کامل