High power single-mode delivery of mid-infrared sources through chalcogenide fiber.
نویسندگان
چکیده
Mechanically robust and low loss single-mode arsenic sulfide fibers are used to deliver high power mid-infrared sources. Anti-reflection coatings were deposited on the fiber facets, enabling 90% transmission through 20 cm length fibers. 10.3 W was transmitted through an anti-reflection coated fiber at 2053 nm, and uncoated fibers sustained 12 MW/cm2 intensities on the facet without failure. A Cr:ZnSe laser transmitted >1 W at 2520 nm, and a Fe:ZnSe laser transmitted 0.5 W at 4102 nm. These results indicate that by improving the anti-reflection coatings and using a high beam quality mid-infrared source, chalcogenide fibers can reliably deliver ≥10 W in a single mode, potentially out to 6.5 µm.
منابع مشابه
Increased mid-infrared supercontinuum bandwidth and average power by tapering large-mode-area chalcogenide photonic crystal fibers.
The trade-off between the spectral bandwidth and average output power from chalcogenide fiber-based mid-infrared supercontinuum sources is one of the major challenges towards practical application of the technology. In this paper we address this challenge through tapering of large-mode-area chalcogenide photonic crystal fibers. Compared to previously reported step-index fiber tapers the photoni...
متن کاملMid-infrared nonlinear absorption in As2S3 chalcogenide glass
We report mid-infrared (MIR) nonlinear absorption in As2S3 glasses which results from two-photon excitation of valence electron to the Urbach extension followed by strong linear absorption of excited states. The measured MIR nonlinear absorption can be 3 to 4 orders of magnitude stronger than the two-photon absorption in the near-infrared for similar laser intensities and does not result from c...
متن کاملHigh-spectral-flatness mid-infrared supercontinuum generated from a Tm-doped fiber amplifier.
Broadband mid-infrared supercontinuum pulses were generated directly from a short piece of active fiber in a single-mode Tm-doped fiber amplifier. The broadband mid-infrared pulses have an extremely high spectral flatness with ~600 nm FWHM bandwidth (from 1.9 μm to 2.5 μm), >15 kW peak power, and >20 GW/cm(2) laser peak intensity. This new approach exhibits a significantly different physical me...
متن کامل2-10 μm Mid-infrared Supercontinuum Generation in As2Se3 Photonic Crystal Fiber
For the first time, we demonstrated that a hyper-broadband from 2μm to 10μm can be generated with a high spectral flatness by using a ~4 um pump and an As2Se3 photonic crystal fiber. The broad and flat dispersion profile and the low guiding loss of the endlessly single-mode As2Se3 photonic crystal fibers combining with the high nonlinearity and wide mid-infrared transparent window of As2Se3 cha...
متن کاملLinear and nonlinear optical properties of chalcogenide microstructured optical fibers
Chalcogenide glasses are known for their large transparency in the mid-infrared and their high linear refractive index (>2). They present also a high non-linear coefficient (n2), 100 to 1000 times larger than for silica, depending on the composition. we have developed a casting method to prepare the microstructured chalcogenide preform. This method allows optical losses as low as 0.4 dB/m at 1....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Optics express
دوره 26 6 شماره
صفحات -
تاریخ انتشار 2018