Combined X-ray and Raman Studies on the Effect of Cobalt Additives on the Decomposition of Magnesium Borohydride
نویسندگان
چکیده
Magnesium borohydride (Mg(BH4)2) is one of the most promising hydrogen storage materials. Its kinetics of hydrogen desorption, reversibility, and complex reaction pathways during decomposition and rehydrogenation, however, present a challenge, which has been often addressed by using transition metal compounds as additives. In this work the decomposition of Mg(BH4)2 ball-milled with CoCl2 and CoF2 additives, was studied by means of a combination of several in-situ techniques. Synchrotron X-ray diffraction and Raman spectroscopy were used to follow the phase transitions and decomposition of Mg(BH4)2. By comparison with pure milled Mg(BH4)2, the temperature for the γ → ε phase transition in the samples with CoF2 or CoCl2 additives was reduced by 10–45 °C. In-situ Raman measurements showed the formation of a decomposition phase with vibrations at OPEN ACCESS Energies 2015, 8 9174 2513, 2411 and 766 cm−1 in the sample with CoF2. Simultaneous X-ray absorption measurements at the Co K-edge revealed that the additives chemically transformed to other species. CoF2 slowly reacted upon heating till ~290 °C, whereas CoCl2 transformed drastically at ~180 °C.
منابع مشابه
Effect of cobalt on structural, microstructural and magnetic properties of magnesium-zinc ferrite nanoparticles
Mg0.5-xCoxZnFe2O4 ferrite nanostructures with various amounts of Co2+ substitution (x= 0, 0.05, 0.10, 0.15) were prepared using a simple and inexpensive sol-gel method sol-gel route. Structural, microstructural and magnetic properties of the prepared powders were investigated by x-ray diffraction (XRD), Fourier transform infrared (FT-IR), field emission- scanning electron microscopy (FE-SEM), X...
متن کاملReversibility and Improved Hydrogen Release of Magnesium Borohydride
Desorption and subsequent rehydrogenation of Mg(BH4)2 with and without 5 mol % TiF3 and ScCl3 have been investigated. Temperature programmed desorption (TPD) experiments revealed a significant increase in the rate of desorption as well as the weight percentage of hydrogen released with additives upon heating to 300 °C. Stable Mg(BxHy)n intermediates were formed at 300 °C, whereas MgB2 was the m...
متن کاملEffect of Additives on Mn/SiO2 Based Catalysts on Oxidative Coupling of Methane
The Oxidative Coupling of Methane (OCM) over M-Na-Mn/SiO2 catalysts (M=W, Cr, Nb and V) was investigated using a continuous-flow quartz reactor at 775°C, 1 atm and 100 cm3min-1 gas flow rates, and correlated with the observed structure and redox properties.The interaction effects of the metal-metal and metal-support on the...
متن کاملPreparation, Characterization, and Investigation of Photocatalytic Activity of TiO2/SiO2/Co Nanocomposite Using Additives
Titanium dioxide has been widely used for photo-catalytic and self-cleaning activities. In this study, TiO2 /SiO2 /Co nanocomposite was prepared by sol-gel method in the presence of Polyvinyl Pyrrolidone (PVP), and Hydroxyl Propyl Cellulose (HPC) as additives, and characterized by IR spectra, Scanning Electron Microscopy (SEM), Energy Dispersive Analytical X-Ray (EDAX), and X-Ray Diffraction (X...
متن کاملIn this paper, the effect of nanocatalytic metal-organic framework based on copper metal and bis-tetrazolamine (CuBTA) ligand functionalized with cobalt (II) oxide nanoparticles on the thermal decomposition behavior of ammonium perchlorate (AP), using differential survey calorimetry (DSC) has been reviewed. First, the metal-organic framework (CuBTA) was synthesized from the raw materials of cop...
متن کامل