The effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the CoNi nanowires
CoNi nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. The effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the CoNi nanowires were investigated. Maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. The coerciv...
متن کاملSuperparamagnetic behavior in ultrathin CoNi layers of electrodeposited CoNi/Cu multilayer nanowires
We present evidence that in a very thin regime the magnetic layers become discrete islands and superparamagnetic in multilayered CoNi 1–17 nm /Cu 4.2 nm nanowires grown by pulsed electrodeposition using a hole pattern of anodized alumina templates. Magnetic hysteresis loops measured at room temperature using a vibrating sample magnetometer show that superparamagnetism appears at t CoNi 1.7 nm, ...
متن کاملEnhanced microwave absorbing performance of CoNi alloy nanoparticles anchored on a spherical carbon monolith.
CoNi alloy nanoparticles anchored on a spherical carbon monolith (CoNi-C) were prepared by a solvothermal route and subsequent heat treatment without any templates. Their permittivity and permeability behaviors were studied in the frequency range of 2-18 GHz. The CoNi-C composites showed the best microwave absorbing performances compared to those of Co-C and Ni-C. The maximum reflection loss of...
متن کاملA soft/hard magnetic nanostructure based on multisegmented CoNi nanowires.
In this paper we have introduced a new soft/hard nanostructure based on multisegmented CoNi nanowire arrays having diameters of around 110 nm and made of five segments with nominal compositions of Co, Co66Ni33, Co50Ni50, Co33Ni66 and Ni, each of which has a length of 800 nm, so that the total length of the multisegmented nanowire is 4 μm. These arrays have been synthesized by means of potentios...
متن کاملElectrodeposited Iron Group Thin-Film Alloys Structure-Property Relationships
Various iron group alloys have been electrodeposited and evaluated for properties including corrosion resistance, microstructure, electrical resistivity, magnetoresistance and other magnetic properties. Corrosion resistance depends on deposit composition and microstructure, which are controlled by solution composition and deposition variables. Maximum corrosion resistance was observed for 50Ni5...