Characterizing and Modeling the Apparent Anomalous Behavior of Resistivity in Cr-Si-O Thin Films
نویسنده
چکیده
منابع مشابه
The Effect of Substrate on Structural and Electrical Properties of Cu3N Thin Film by DC Reactive Magnetron Sputtering
The aim of this paper is to study the effect of substrate on the Cu3N thin films. At first Cu3N thin films are prepared using DC magnetron sputtering system. Then structural properties, surface roughness, and electrical resistance are studied using X-ray diffraction (XRD), the atomic force microscope (AFM) and four-point probe techniques respectively. Finally, the results are investigated and c...
متن کاملSoft Magnetic Properties of High-Entropy Fe-Co-Ni-Cr-Al-Si Thin Films
Soft magnetic properties of Fe-Co-Ni-Al-Cr-Si thin films were studied. As-deposited Fe-Co-Ni-Al-Cr-Si nano-grained thin films showing no magnetic anisotropy were subjected to field-annealing at different temperatures to induce magnetic anisotropy. Optimized magnetic and electrical properties of Fe-Co-Ni-Al-Cr-Si films annealed at 200 ◦C are saturation magnetization 9.13 × 105 A/m, coercivity 79...
متن کاملDevelopments of the Physical and Electrical Properties of NiCr and NiCrSi Single-Layer and Bi-Layer Nano-Scale Thin-Film Resistors
In this study, commercial-grade NiCr (80 wt % Ni, 20 wt % Cr) and NiCrSi (55 wt % Ni, 40 wt % Cr, 5 wt % Si) were used as targets and the sputtering method was used to deposit NiCr and NiCrSi thin films on Al₂O₃ and Si substrates at room temperature under different deposition time. X-ray diffraction patterns showed that the NiCr and NiCrSi thin films were amorphous phase, and the field-effect s...
متن کاملZnO Nanowires/Nanobelts Structured CO Gas Sensor
Zinc oxide nanowires/nanobelts thin films were prepared by thermal evaporation deposition of Zn on two different kinds of substrates, namely Cr-glass and Cr-<100> n-type Si. ZnO nanostructured based COgas sensing thin films were formed, and the morphologies of these films were investigated by scanning electron microscopy (SEM). The sensing response of the films toward CO gas at operating temper...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کامل