Room-Temperature Freeze Casting for Ceramics with Nonaqueous Sublimable Vehicles in the Naphthalene–Camphor Eutectic System
نویسندگان
چکیده
Freeze casting for Al2O3 was accomplished at room temperature with nonaqueous sublimable vehicles in the naphthalene– camphor eutectic system with a eutectic temperature of 31°C. A fully dense sintered body (>99.5% of theoretical density (T.D.)) was obtained with a eutectic composition vehicle, whereas at most 90% T.D. was obtained with an off-eutectic (i.e., hypoor hypereutectic) composition vehicle due to formation of large uniquely shaped voids. Microstructural observation suggested that growing pro-eutectic crystals rejected the suspended Al2O3 particles to form large voids during the solidification process. At the eutectic composition, formation of fine lamellar microstructure in a solidified vehicle is considered to inhibit particle rejection resulting in large voids.
منابع مشابه
Preparation of aliened porous Ni-GDC nano composite by freeze-casting process
This current study reports preparation of Nickel-Gadolinium doped Ceria (Ni-GDC) composite via controlled unidirectional freeze casting of aqueous-based GDC slurry completed with nickel infiltrated into the porous GDC samples. Gadolinium doped ceria powder prepared by gel-combustion synthesis method. The oxide powder was confirmed to be the fluorite-structured of Ce0.8Gd0.2O1.9 solid solution b...
متن کاملDeep Eutectic Solvent Based on Choline Chloride/Urea as an Efficient Catalytic System for the One-Pot Synthesis of Highly Functionalized 1,4-Dihydropyridines and Polysubstituted 4H-Chromenes
One-pot four-component synthesis of polyfunctionalized 1,4-dihydropyridine derivatives was developed by a condensation of aldehydes, malononitrile, diethylacetylenedicarboxylate and aniline in the presence of choline chloride/urea as a deep eutectic solvent (DES)at room temperature.Moreover, an efficient method was reported for the synthesis of highly substituted 4H-chromenes through one-...
متن کاملEthanol-based Tape Casting Process of the Textured Bi0.5(Na0.80K0.20)0.5TiO3-BiFeO3 Ceramics
The rheological and tape casting behavior of ethanol-based Bi0.5(Na0.80K0.20)0.5TiO3-7 mol% BiFeO3 (BNKT-BF) slurries was investigated. The effect of sintering temperature profile on texture development with a preferred orientation was also studied. A 50 MPa pressure assisted three step sintering profile promoted extensive texture development together with densification. The role of BF as a sin...
متن کاملEffect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
متن کاملResidual Stresses in Novel Metal/ceramic Composites Exhibiting a Lamellar Microstructure
The aim of this study is to analyze the mechanics of a new class of metal/ceramic composite on a mesoscopic length scale. These composites are produced by melt infiltration of porous ceramic preforms produced by freeze-casting and subsequent sintering. This production route has a high application potential since it offers a cost-effective way to obtain composites with ceramic content in the ran...
متن کامل