Synthesis and characterization of antibacterial polyurethane coatings from quaternary ammonium salts functionalized soybean oil based polyols.
نویسندگان
چکیده
In this study, a simple and versatile synthetic approach was developed to prepare bactericidal polyurethane coatings. For this purpose, introduction of both quaternary ammonium salts (QASs), with well-known antibacterial activity, and reactive hydroxyl groups on to the backbone of soybean oil was considered. Epoxidized soybean oil was reacted with diethylamine and the intermediate tertiary amine containing polyol was reacted with two different alkylating agents, methyl iodide and benzyl chloride, to produce MQAP and BQAP, respectively. These functional polyols were reacted with different diisocyanate monomers to prepare polyurethane coatings. Depending on the structure of monomers used for the preparation of polyurethane coatings, initial modulus, tensile strength and elongation at break of samples were in the ranges of 122-339 MPa, 4.6-12.4 MPa and 8.4-46%, respectively. Polyurethane coatings based on isophorone diisocyanate showed proper mechanical properties and adhesion strength (0.41 MPa) for coating application. Study of fibroblast cells interaction with prepared polyurethanes showed promising cells viability in the range of 78-108%. Meanwhile, MQAP based samples with higher concentration of QASs showed better adhesion strength, surface hydrophilicity and antibacterial activity (about 95% bacterial reduction). Therefore, these materials can find applications as bactericidal coating for biomedical devices and implants.
منابع مشابه
Synthesis and characterization of polyurethanes made from copolymers of epoxidized natural oil and tetrahydrofuran.
Polyols were synthesized from epoxidized natural oils and tetrahydrofuran through ring opening copolymerization catalyzed by Lewis acid. The properties of these polyols depend on the type of natural oils as well as the reaction conditions (monomer concentration, catalyst amount, reaction temperature and reaction time). These polyols were evaluated as a raw material for making polyurethane (PU) ...
متن کاملPreparation and Characterization of Soybean Oil-Based Polyurethanes for Digital Doming Applications
Polyurethane-resin doming is currently one of the fastest growing markets in the field of industrial graphics and product identification. Semi-rigid bio-based polyurethanes were prepared deriving from soybean oil as a valuable alternative to fossil materials for digital doming and applied to digital mosaic technology. Bio-resins produced can favorably compete with the analogous fossil polymers,...
متن کاملSynthesis and antibacterial activity of quaternary ammonium salt-type antibacterial agents with a phosphate group.
Quaternary ammonium salts are frequently used as antibacterial agent that disrupts cell membrane through the binding of their ammonium cations to anionic sites in the outer layer tissue of bacteria. This article describes the synthesis of quaternary ammonium salt-type antibacterial agents with a phosphate group that strongly binds to hydroxyapatite and bromide ion as counterion. Evaluation of t...
متن کاملQuaternary Ammonium Salts of Poly(N,N-dimethylaminoethyl methacrylate) as an Efficient Antibacterial Agent for Polylactide Textiles
متن کامل
Polyol from castor oil and epoxy resin for PU Coatings
Novel reactive polyols were synthesized via modification of castor oil, a renewable agricultural raw material with epoxy resin and triethylamine as a catalyst. This polyol was used for synthesis of polyurethane coating. Coating formulations were developed by reacting polyol with aromatic adduct, aliphatic adduct and castor oil based adduct in different NCO/OH ratio. All coating composition syst...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Materials science & engineering. C, Materials for biological applications
دوره 33 1 شماره
صفحات -
تاریخ انتشار 2013