Tribocorrosion Failure Mechanism of TiN/SiOx Duplex Coating Deposited on AISI304 Stainless Steel

نویسندگان

  • Qiang Chen
  • Zhiwen Xie
  • Tian Chen
  • Feng Gong
چکیده

TiN/SiOx duplex coatings were synthesized on AISI304 stainless steel by plasma immersion ion implantation and deposition (PIIID) followed by radio frequency magnetron sputtering (RFMS). The microstructure and tribocorrosion failure behaviors of the duplex coatings were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, atomic force microscopy, reciprocating-sliding tribometer, and electrochemical tests. The as-deposited duplex coating had a two-layered columnar growth structure consisting of face-centered cubic TiN and amorphous SiOx. Sliding tests showed that the TiN interlayer had good adhesion with the substrate, but the SiOx layer suffered from severe delamination failure. Friction force induced a number of micro-cracks in the coating, which provided channels for the diffusion of NaCl solution. The tribocorrosion test showed that the duplex coating exhibited a lower wear-performance in NaCl solution than in ambient atmosphere. Multi-scale chloride ion corrosion occurred simultaneously and substantially degraded the bonding strength of the columnar crystals or neighboring layers. Force-corrosion synergy damage eventually led to multi-degradation failure of the duplex coating. The presented results provide a comprehensive understanding of the tribocorrosion failure mechanism in coatings with duplex architecture.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Self-Cleaning Properties of TiN/CrN Nanoscale Multi-layer Deposited on Surgical 420C Stainless Steel

The present paper focuses on the investigation of self-cleaning properties based on studding of water repellency and blood repellency for TiN- and CrN single-layer and TiN/CrN nanoscale multi-layer coatings deposited via Cathodic Arc Evaporation (CAE) method on medical grade 420C stainless steel substrate. X-ray diffraction (XRD) method and Field Emission Scanning Electron Microscope (FESEM) wa...

متن کامل

Prediction of surface roughness and cutting zone temperature in dry turning processes of AISI304 stainless steel using ANFIS with PSO learning

This paper presents an approach for modeling and prediction of both surface roughness and cutting zone temperature in turning of AISI304 austenitic stainless steel using multi-layer coated (TiCN+TiC+TiCN+TiN) tungsten carbide tools. The proposed approach is based on an adaptive neuro-fuzzy inference system (ANFIS) with particle swarm optimization (PSO) learning. AISI304 stainless steel bars are...

متن کامل

Investigation of failure mode of similar and dissimilar joint of duplex stainless steel bye resistance spot welding in Shear-tensile conditions

The present study investigates the failure resistance welding method of a similar and unmatched connection point in duplex stainless steel under shear stress conditions. In this study, 1Cr21Ni5Ti branded stainless steel duplex was used. Micro-hardness test, tensile test - cutting and optical metallography to describe the macrostructure and microstructure, hardness button welding and weld failur...

متن کامل

Temperature Dependence of Residual Stress in Tin Films on 316 Stainless Steel

The residual stresses in a TiN film deposited by a reactive ion coating process on a 316 stainless steel sheet were determined by the sin$ X-ray diffraction method, at temperatures from 15-800 “C. Using specially designed nickel clips, the coated strip was heated by the passage of a resistive current, in conjunction with a surround heater, and the temperature was measured by a Pt/Pt-lO%Rh therm...

متن کامل

High temperature wear and frictional properties of duplex-treated tool steel sliding against a two phase brass

Improvement of die life in the hot forging of brass alloys is considered vital from both technical and economical points of view. In this research, pin-ondisc tests were carried out at a range of temperatures to evaluate the influence of plasma nitriding and duplex nitriding-physical vapour deposition (PVD), including TiN-TiAlN and TiN-TiAlN-CrAlN coatings, on the tribological properties of AIS...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 9  شماره 

صفحات  -

تاریخ انتشار 2016