Room temperature multiplexed gas sensing using chemical-sensitive 3.5-nm-thin silicon transistors
نویسندگان
چکیده
There is great interest in developing a low-power gas sensing technology that can sensitively and selectively quantify the chemical composition of a target atmosphere. Nanomaterials have emerged as extremely promising candidates for this technology due to their inherent low-dimensional nature and high surface-to-volume ratio. Among these, nanoscale silicon is of great interest because pristine silicon is largely inert on its own in the context of gas sensing, unless functionalized with an appropriate gas-sensitive material. We report a chemical-sensitive field-effect transistor (CS-FET) platform based on 3.5-nm-thin silicon channel transistors. Using industry-compatible processing techniques, the conventional electrically active gate stack is replaced by an ultrathin chemical-sensitive layer that is electrically nonconducting and coupled to the 3.5-nm-thin silicon channel. We demonstrate a low-power, sensitive, and selective multiplexed gas sensing technology using this platform by detecting H2S, H2, and NO2 at room temperature for environment, health, and safety in the oil and gas industry, offering significant advantages over existing technology. Moreover, the system described here can be readily integrated with mobile electronics for distributed sensor networks in environmental pollution mapping and personal air-quality monitors.
منابع مشابه
Photo-Induced Room-Temperature Gas Sensing with a-IGZO Based Thin-Film Transistors Fabricated on Flexible Plastic Foil
We present a gas sensitive thin-film transistor (TFT) based on an amorphous Indium-Gallium-Zinc-Oxide (a-IGZO) semiconductor as the sensing layer, which is fabricated on a free-standing flexible polyimide foil. The photo-induced sensor response to NO₂ gas at room temperature and the cross-sensitivity to humidity are investigated. We combine the advantages of a transistor based sensor with flexi...
متن کاملCarrier Transport in Ultra-Thin Nano/Polycrystalline Silicon Films and Nanowires
Carrier transport was investigated in two different types of ultra-thin silicon films, polycrystalline silicon (poly-Si) films with large grains > 20 nm in size and hydrogenated nanocrystalline silicon (nc-Si:H) films with grains 4 nm – 8 nm in size. It was found that there were local non-uniformities in grain boundary potential barriers in both types of films. Single-electron charging effects ...
متن کاملVisible photoassisted room-temperature oxidizing gas-sensing behavior of Sn2S3 semiconductor sheets through facile thermal annealing
Well-crystallized Sn2S3 semiconductor thin films with a highly (111)-crystallographic orientation were grown using RF sputtering. The surface morphology of the Sn2S3 thin films exhibited a sheet-like feature. The Sn2S3 crystallites with a sheet-like surface had a sharp periphery with a thickness in a nanoscale size, and the crystallite size ranged from approximately 150 to 300 nm. Postannealing...
متن کاملRoom Temperature and Reduced Pressure Chemical Vapor Deposition of Silicon Carbide on Various Materials Surface
At room temperature, 300 K, silicon carbide film was formed using monomethylsilane gas on the reactive surface prepared using argon plasma. Entire process was performed at reduced pressure of 10 Pa in the argon plasma etcher, without a substrate transfer operation. By this process, the several-nanometer-thick amorphous thin film containing silicon-carbon bonds was obtained on various substrates...
متن کاملExcited states and quantum confinement in room temperature few nanometre scale silicon single electron transistors.
Single nanometre scale quantum dots (QDs) have significant potential for many 'beyond CMOS' nanoelectronics and quantum computation applications. The fabrication and measurement of few nanometre silicon point-contact QD single-electron transistors are reported, which both operate at room temperature (RT) and are fabricated using standard processes. By combining thin silicon-on-insulator wafers,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 3 شماره
صفحات -
تاریخ انتشار 2017