Synthesis and Luminescence Properties of Core/Shell ZnS:Mn/ZnO Nanoparticles
نویسندگان
چکیده
In this paper the influence of ZnO shell thickness on the luminescence properties of Mn-doped ZnS nanoparticles is studied. Transmission electron microscopy (TEM) images showed that the average diameter of ZnS:Mn nanoparticles is around 14 nm. The formation of ZnO shells on the surface of ZnS:Mn nanoparticles was confirmed by X-ray diffraction (XRD) patterns, high-resolution TEM (HRTEM) images, and X-ray photoelectron spectroscopy (XPS) measurements. A strong increase followed by a gradual decline was observed in the room temperature photoluminescence (PL) spectra with the thickening of the ZnO shell. The photoluminescence excitation (PLE) spectra exhibited a blue shift in ZnO-coated ZnS:Mn nanoparticles compared with the uncoated ones. It is shown that the PL enhancement and the blue shift of optimum excitation wavelength are led by the ZnO-induced surface passivation and compressive stress on the ZnS:Mn cores.
منابع مشابه
Effects of the Template Composition and Coating on the Photoluminescence Properties of ZnS:Mn Nanoparticles
Mn-doped ZnS nanocrystals based on low dopant concentrations (0-2%) and coated with a shell of Zn(OH)2 have been prepared via soft template and precipitation reaction. The results indicate that the ZnS:Mn nanocrystal is cubic zinc blende structure and its diameter is 3.02 nm as demonstrated by XRD. Measured by TEM, the morphology of nanocrystals is a spherical shape, and their particle size (3-...
متن کاملEnhanced UV Emission From Silver/ZnO And Gold/ZnO Core-Shell Nanoparticles: Photoluminescence, Radioluminescence, And Optically Stimulated Luminescence
The optical properties of core-shell nanoparticles consisting of a ZnO shell grown on Ag and Au nanoparticle cores by a solution method have been investigated. Both the ZnO/Ag and ZnO/Au particles exhibit strongly enhanced near-band-edge UV emission from the ZnO when excited at 325 nm. Furthermore, the UV intensity increases with the metal nanoparticle concentration, with 60-fold and 17-fold en...
متن کاملSynthesis and luminescence properties of ZnS:Mn/ZnS core/shell nanorod structures
Mn-doped ZnS nanorods synthesized by solvothermal method were successfully coated with ZnS shells of various thicknesses. The powder X-ray diffraction (XRD) measurements showed the ZnS:Mn nanorods were wurtzite structure with preferential orientation along c-axis. Transmission electron microscopy images (TEM) revealed that the ZnS shells formed from small particles, growing along a-axis orienta...
متن کاملSol-gel Synthesis of ZnO Nanoparticles and ZnO-TiO2-SiO2 Nanocomposites and Their Photo-catalyst Investigation in Methylene Blue Degradation
In this work firstly ZnO nanoparticles were synthesized via a simple precipitation method. At the second step titanium dioxide and silicon dioxide shell were synthesized on the core. For preparation ZnO-TiO2-SiO2 the sol product was calcinated at 500 ºC for 2h. Properties of the product were examined by X-raydiffraction pattern (XRD), scanning electron microscope (SEM) and Fourier transform inf...
متن کاملAn Investigation on Synthesis and Magnetic Properties of Manganese Doped Cobalt Ferrite Silica Core-Shell Nanoparticles for Possible Biological Application
In this work, we investigated synthesis, magnetic properties of silica coated metal ferrite, (CoFe2O4)/SiO2 and Manganese doped cobalt ferrite nanoparticles (MnxCo1-xFe2O4 with x= 0.02, 0.04 and 0.06)/SiO2 for possible biomedical application. All the ferrites nanoparticles were prepared by co-precipitation method using FeCl3.6H2O, CoCl2.6H2O and MnCl2.2H2O as precursors, and were silica coated ...
متن کامل