Mesoporous hexagonal Co3O4 for high performance lithium ion batteries
نویسندگان
چکیده
Mesoporous Co3O4 nanoplates were successfully prepared by the conversion of hexagonal β-Co(OH)2 nanoplates. TEM, HRTEM and N2 sorption analysis confirmed the facet crystal structure and inner mesoporous architecture. When applied as anode materials for lithium storage in lithium ion batteries, mesoporous Co3O4 nanocrystals delivered a high specific capacity. At 10 C current rate, as-prepared mesoporous Co3O4 nanoplates delivered a specific capacity of 1203 mAh/g at first cycle and after 200 cycles it can still maintain a satisfied value (330 mAh/g). From ex-situ TEM, SAED and FESEM observation, it was found that mesoporous Co3O4 nanoplates were reduced to Li2O and Co during the discharge process and re-oxidised without losing the mesoporous structure during charge process. Even after 100 cycles, mesoporous Co3O4 crystals still preserved their pristine hexagonal shape and mesoporous nanostructure.
منابع مشابه
Hierarchically ordered mesoporous Co3O4 materials for high performance Li-ion batteries
Highly ordered mesoporous Co3O4 materials have been prepared via a nanocasting route with three-dimensional KIT-6 and two-dimensional SBA-15 ordered mesoporous silicas as templates and Co(NO3)2 · 6H2O as precursor. Through changing the hydrothermal treating temperature of the silica template, ordered mesoporous Co3O4 materials with hierarchical structures have been developed. The larger pores a...
متن کاملHighly ordered mesoporous Cr2O3 materials with enhanced performance for gas sensors and lithium ion batteries.
Highly ordered mesoporous Cr(2)O(3) materials with high specific surface area and narrow pore size distribution were successfully prepared by a vacuum assisted impregnation method. Both 2-dimensional hexagonal and 3-dimensional cubic Cr(2)O(3) mesoporous replicas from SBA-15 and KIT-6 templates exhibit enhanced performance for gas sensors and lithium ion batteries, compared to the bulk Cr(2)O(3...
متن کاملMetal coordination polymer derived mesoporous Co3O4 nanorods with uniform TiO2 coating as advanced anodes for lithium ion batteries.
In this work, a one-dimensional Co3O4@TiO2 core-shell electrode material with superior electrochemical performance is fabricated by a convenient and controllable route. The approach involves two main steps: the homogeneous deposition of polydopamine and TiO2 layers in sequence on the cobalt coordination polymer and the thermal decomposition of the polymer matrix. The as-prepared electrode mater...
متن کاملEnvironmental-Friendly and Facile Synthesis of Co3O4 Nanowires and Their Promising Application with Graphene in Lithium-Ion Batteries
In this work, we developed an eco-friendly strategy for preparing Co3O4 nanowires. The process consisted of two steps: controllable synthesis of metal cobalt nanowires followed by a facile air-oxidization step. The 1D nanowire structure with a high aspect ratio was easily achieved via a magnetic-field-assisted self-assembly of cobalt ion complexes during reduction. After air-calcinations, the C...
متن کاملRectangular Co3O4 with micro-/nanoarchitectures: charge-driven PDDA-assisted synthesis and excellent lithium storage performance.
For the first time, two dimensional (2D) rectangular Co3O4 with micro-/nanoarchitectures is successfully synthesized by a facile hydrothermal treatment with the assistance of poly(diallyldimethylammonium chloride) (PDDA). Owing to the strong electrostatic interaction, positively charged PDDA molecules are considered as structure directing agents and play a crucial role in the formation of the u...