Effect of Different Current Values on Microstructure and Mechanical Properties of Microalloyed Steels Joined by the Submerged Arc Welding Method
نویسندگان
چکیده
In this study, microalloyed steels were joined by using the submerged arc welding method at different welding currents of 350 A, 400 A and 450 A. The effects of selected welding parameters on the microstructure and mechanical properties of welded materials were investigated. Tensile tests and microhardness measurements were performed. Microstructural changes have been identified in the welding zone. The results showed an increase in hardness and tensile strength depending on the current intensity. The heat affected zone was observed much wider with the increase in welding current.
منابع مشابه
Effect of Inclusions on Acicular Ferrite Formation in Submerged Arc Welding of API5L-X65
In the present study, effect of inclusions characteristics changing on the formation of acicular ferrite in submerged arc welding of API5l-X65 low alloy steel was investigated. Three different welding fluxes with different chemical composition and basicity index of 0.72, 0.82 and 0.99, and two different welding heat inputs of 1.6 kJ / mm and 2.4 kJ / mm were used to create inclusions with diffe...
متن کاملEffect of Inclusions on Acicular Ferrite Formation in Submerged Arc Welding of API5L-X65
In the present study, effect of inclusions characteristics changing on the formation of acicular ferrite in submerged arc welding of API5l-X65 low alloy steel was investigated. Three different welding fluxes with different chemical composition and basicity index of 0.72, 0.82 and 0.99, and two different welding heat inputs of 1.6 kJ / mm and 2.4 kJ / mm were used to create inclusions with diffe...
متن کاملThe Effect of Two-stage Heat Treatment Temperatures on Initial and FSSWed Properties of TRIP Steels
In this paper, a 0.2 C–1.6 Mn–1.5 Si wt. % TRIP-aided cold-rolled steel sheet was fabricated and the optimal heat treatment conditions (Intercritical Annealing “IA” and Bainitic Isothermal Transformation “BIT”) were investigated to maximize the volume fraction and stability of the retained austenite. The effects of temperature on IA (770, 790 and 810 ºC) and BIT (330, 350 and 370 <su...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کامل