Influence of nonadiabatic annealing on the morphology and molecular structure of PEDOT-PSS films.
نویسندگان
چکیده
The effect of nonadiabatic annealing on poly(3,4-ethylendioxythiophene)-poly(styrenesulfonate) (PEDOT-PSS) thin films prepared on silicon substrate has been investigated by Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). The analysis indicates the formation of an annealing-induced doping in PEDOT structure, suggesting a modification of the polymer electronic structure and the formation of a PEDOT-rich film surface.
منابع مشابه
Influence of annealing on anisotropic crystalline structure of HDPE cast films
High density polyethylene (HDPE) films were produced using cast film extrusion process with different draw ratios, ranging from 16.9 to 148.8. Morphology, crystallinty and orientation state of crystalline and amorphous phases of the cast films were investigated using scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and polarized Fourier transform infrared spectroscopy...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کاملNano-structural Characterization of Post-annealed ZnO Thin Films by X-ray Diffraction and Field Emission Scanning Electron Microscopy
ZnO thin films were deposited on Si(400) substrates by e-beam evaporation technique, and then post-annealed at different annealing temperatures (200-800°C). Dependence of the crystallographic structure, nano-strain, chemical composition and surface physical Morphology of these layers on annealing temperature were studied. The crystallographic structure of films was studied using X-Ray Diffracti...
متن کاملFormation of Cupric Oxide Films on Quartz Substrates by Annealing the Copper Films
In the present work, cupric oxide (CuO) films were obtained through thermal annealing of the copper (Cu) films deposited on quartz substrates by DC magnetron sputtering method. The annealing was performed in air atmosphere for different times ranging from 60-240 min at temperature of 400 ºC. The influence of annealing times on structural and morphological properties of the films was investi...
متن کاملSTUDY OF ANNEALING TEMPERATURE VARIATION ON THE STRUCTURAL PROPERTIES OF DIP-COATED TiO2-SiO2 NANOSTRUCTURED FILMS
Abstract:In the present research, SiO2–TiO2 nanostructure films were successfully prepared on windshields using the sol–gel technique for photocatalytic applications. To prevent the thermal diffusion of the sodium ions from the glass to TiO2 films, the SiO2 layer was pre-coated on the glass by the sol–gel method. The substrates were dipped in the sol and withdrawn with the speed of 6cm/min-1 to...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- The journal of physical chemistry. B
دوره 113 28 شماره
صفحات -
تاریخ انتشار 2009