MAGNETOSTRICTION CONSTANT OF MULTILAYER Ni-Ag FILMS DETERMINED BY FERROMAGNETIC RESONANCE

نویسندگان

  • R. Żuberek
  • H. Szymczak
  • R. Krishnan
  • M. Tessier
چکیده

The results of magnetostriction constant A, of multilayer Ni-Ag films are reported. The measurements have been performed at room temperature using strain modulated ferromagnetic resonance method. The magnetostriction constant As depends linearly on the inverse Ni layer thickness. This effect is suggested to be due to the reduced local symmetry in interfaces.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Origin of room-temperature perpendicular magnetic anisotropy in Ni/Pt multilayers

Room-temperature perpendicular magnetic anisotropy ~PMA! was observed in Ni/Pt multilayer films having 7–30 Å Ni and constant 3 Å Pt sublayer thickness, prepared by magnetron sputtering at an Ar sputtering pressure of 7 mTorr. To understand the origin of PMA, the magnetoelastic anisotropy was determined from delicate in situ stress and ex situ magnetostriction coefficient measurements. Tensile ...

متن کامل

Ferromagnetic resonance study of sputtered Co | Ni multilayers

We report on room temperature ferromagnetic resonance (FMR) studies of [t Co|2t Ni]×N sputtered films, where 0.1 ≤ t ≤ 0.6 nm. Two series of films were investigated: films with same number of Co|Ni bilayer repeats (N=12), and samples in which the overall magnetic layer thickness is kept constant at 3.6 nm (N=1.2/t). The FMR measurements were conducted with a high frequency broadband coplanar wa...

متن کامل

Observation of thickness dependence of magnetic surface anisotropy in ultrathin amorphous films.

Ferromagnetic resonance (FMR) and SQUID magnetometry measurements have been made on multilayers of amorphous FeioB30/Ag. The dependence of the magnetic surface anisotropy constant K, on the magnetic layer thickness 2L has been determined in the range 1.6 A ( 2L & 90 A using more than twenty samples. It is found that K, is constant for 2L ) 16.S A, but decreases monotonically towards zero as 2L ...

متن کامل

Magnetostrictive thin films for microwave spintronics

Multiferroic composite materials, consisting of coupled ferromagnetic and piezoelectric phases, are of great importance in the drive towards creating faster, smaller and more energy efficient devices for information and communications technologies. Such devices require thin ferromagnetic films with large magnetostriction and narrow microwave resonance linewidths. Both properties are often degra...

متن کامل

Room-temperature perpendicular magnetic anisotropy in Ni/Pd „111... multilayers

We report the experimental observation of room-temperature perpendicular magnetic anisotropy ~PMA! in Ni/Pd ~111! multilayer films having the thickness range of 5–11 Å Ni and 4–11 Å Pd sublayers, prepared by direct current magnetron sputtering on glass substrates at Ar sputtering pressure of 7 mTorr. Perpendicular magnetic anisotropy was found to be sensitively dependent on both Niand Pd-sublay...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2016