Measurement of release wave speed in shockcompressed polycrystalline alumina and aluminum
نویسنده
چکیده
Values of release wave speed in shock-compressed polycrystalline alumina and aluminum (2024) have been measured to 400 and 260 kbar, respectively. These values, as well as previous data for aluminum and iron, have been compared with fourth-order finite strain extrapolations of the longitudinal sound speed V o. For alumina in the pressure range 200-300 kbar and for a iron and • iron the observed release wave speeds fall below any reasonable extrapolation of Vo. In the range 360-400 kbar the data for alumina indicate that M(O2M/• P•) --50 (where M and P are longitudinal modulus and pressure, respectively); this value is in approximate agreement with Graham's ,-•200-kbar data on elastic shock compression of single-crystal aluminum oxide. For aluminum the data indicate a value for M(•2M/•P •) of 2.7 45.7.
منابع مشابه
New sol-gel derived aluminum oxide-ibuprofen nanocomposite as a controlled releasing medication
Objective(s): In a new approach, following the development in metal oxide chemistry, the ibuprofen as low water soluble nonsteroidal anti-inflammatory drug diffused into synthetic sol-gel derived nano porous g-alumina by an impregnation method in order to increase the solubility and control the drug release in physiological environment. Methods: Sol-gel m...
متن کاملStudies on Thermal Decomposition of Aluminium Sulfate to Produce Alumina Nano Structure
Aluminum sulfate nano structures have been prepared by solution combustion synthesis using aluminum nitrate nonahydrate (Al(NO3)3.9H2O) and ammonium sulfate ((NH4)2SO4). The resultant aluminum sulfate nano structures were calcined at different temperatures to study thermal decomposition of aluminum sulfate. The crystallinity and phase of the as-synthesized and calcined samples were char...
متن کاملThe wetting behavior of NiAl and NiPtAl on polycrystalline alumina
In order to understand the beneficial effect of Pt on the adherence of thermally grown alumina scales, sessile drop experiments were performed to study the wetting of poly-crystalline alumina by nickel-aluminum alloys with or without platinum addition where the amount of Pt ranged from 2.4 to 10 at.%. Subsequent interfacial structure was evaluated using atomic force microscopy. Platinum additio...
متن کاملThe development of a thermal diffusivity reference material using alumina
Polycrystalline alumina developed by the Japan Fine Ceramics Center (JFCC) has been studied as a candidate thermal diffusivity reference material. It was experimentally confirmed that the alumina developed by the JFCC is homogeneous and stable enough to be used as a reference material. The thermal diffusivities of two specimens of different thicknesses (2 and 3 mm) were measured by the laser fl...
متن کامل