Rapid Synthesis of Thin and Long Mo17O47 Nanowire-Arrays in an Oxygen Deficient Flame
نویسندگان
چکیده
Mo17O47 nanowire-arrays are promising active materials and electrically-conductive supports for batteries and other devices. While high surface area resulting from long, thin, densely packed nanowires generally leads to improved performance in a wide variety of applications, the Mo17O47 nanowire-arrays synthesized previously by electrically-heated chemical vapor deposition under vacuum conditions were relatively thick and short. Here, we demonstrate a method to grow significantly thinner and longer, densely packed, high-purity Mo17O47 nanowire-arrays with diameters of 20-60 nm and lengths of 4-6 μm on metal foil substrates using rapid atmospheric flame vapor deposition without any chamber or walls. The atmospheric pressure and 1000 °C evaporation temperature resulted in smaller diameters, longer lengths and order-of-magnitude faster growth rate than previously demonstrated. As explained by kinetic and thermodynamic calculations, the selective synthesis of high-purity Mo17O47 nanowires is achieved due to low oxygen partial pressure in the flame products as a result of the high ratio of fuel to oxidizer supplied to the flame, which enables the correct ratio of MoO2 and MoO3 vapor concentrations for the growth of Mo17O47. This flame synthesis method is therefore a promising route for the growth of composition-controlled one-dimensional metal oxide nanomaterials for many applications.
منابع مشابه
The Effects of Different Seed Layers and Growth Time on the Quality of ZnO NRs Arrays
ZnO nanorods (NRs) were synthesized using an in situ low-temperature hydrothermal method. In order to investigate the effect of different seed layers on quality of ZnO NRs arrays, alcoholic, alkaline and acidic seed solutions were deposited by spin coating on ITO-glass substrate. Experimental results revealed that the vertically ZnO NRs obtained from monoethanolamine-based seed layer is the...
متن کاملAAO-assisted synthesis of highly ordered, large-scale TiO2 nanowire arrays via sputtering and atomic layer deposition
Highly ordered nanoporous anodic aluminum oxide (AAO) thin films were fabricated in oxalic acid under a constant voltage via a two-step anodization process. To investigate the high-aspect-ratio (7.5:1) filling process, both sputtering and atomic layer deposition (ALD) were used to form TiO2 nanowires. Field emission scanning electron microscopy and high-resolution transmission electron microsco...
متن کاملControllable synthesis of branched ZnO/Si nanowire arrays with hierarchical structure
A rational approach for creating branched ZnO/Si nanowire arrays with hierarchical structure was developed based on a combination of three simple and cost-effective synthesis pathways. The crucial procedure included growth of crystalline Si nanowire arrays as backbones by chemical etching of Si substrates, deposition of ZnO thin film as a seed layer by magnetron sputtering, and fabrication of Z...
متن کاملArrays of indefinitely long uniform nanowires and nanotubes.
Nanowires are arguably the most studied nanomaterial model to make functional devices and arrays. Although there is remarkable maturity in the chemical synthesis of complex nanowire structures, their integration and interfacing to macro systems with high yields and repeatability still require elaborate aligning, positioning and interfacing and post-synthesis techniques. Top-down fabrication met...
متن کاملSpontaneous growth of superstructure alpha-Fe2O3 nanowire and nanobelt arrays in reactive oxygen plasma.
One-dimensional a-Fe2O3 is a promising nanomaterial for advanced applications in catalysis and water splitting, environmental protection, sensors, dye solar cells, magnetic storage media, bioprocessing, and controlled drug delivery and detection, especially as carriers of antigens for prion detection and PCR manipulation. a-Fe2O3 nanowires have been successfully synthesized by various methods b...
متن کامل