Studies of third-order nonlinearities in materials and devices for ultrafast lasers
نویسنده
چکیده
Recent developments in telecommunications, frequency metrology, and medical imaging have motivated research in ultrafast optics. Demand exists for broadband components and sources as well as highly nonlinear fibers and materials. For this thesis, several different devices have been developed for such applications. Broadband saturable absorbers based on III/V and Si materials systems were developed for femtosecond lasers and have high reflectivity over 200 to 300 nm bandwidths. These absorbers were designed for modulation depths ranging from 0.3% to 18%. Self-starting modelocked operation with the absorbers was achieved in a variety of lasers including Ti:Sapphire, Cr:Forsterite, Er:glass, Cr4+:YAG and erbium-doped bismuth-oxide fiber. In tapered microstructure fiber, highly nondegenerate four-wave mixing was achieved, with a frequency shift of 6000 cm-1 in an interaction length of only 1.4 cm. Amplification in erbium-doped bismuth-oxide fiber was demonstrated, with gains of 12 dB achieved between 1520 1600 nm in a 22.7-cm length. With a 55.6 cm length of bismuthoxide erbium-doped fiber, an L-band modelocked laser was constructed, tunable between 1570 1600 nm. It produced 288-fs pulses at 1600 nm. Undoped highly nonlinear bismuthoxide fiber was used to generate smooth, controlled supercontinuum between 1200 to 1800 nm. Pulse compression of 150-fs pulses to 25 fs was also demonstrated. Finally, the nonlinear refractive index coefficient and two-photon absorption coefficient of Ge-As-Se glasses were measured. Ge35As15Se50 is found to have a nonlinearity 900 times that of silica. Thesis Supervisor: Erich P. Ippen Title: Professor of Physics, Elihu Thompson Professor of Electrical Engineering Professor of Physics
منابع مشابه
Femtosecond all-optical devices for ultrafast communication and signal processing
Future bandwidth demand in optical communication and signal processing systems will soon exceed 100 Gb s−1 as is commonly forecasted from a throughput experience curve for communication systems. However, such systems cannot be realized without introducing ultrafast, all-optical devices, since existing optoelectronic and electronic devices and integrated circuits would not be able to function at...
متن کاملPhotonic Materials and Devices
Our recent advances in solid-state optoelectronic materials and devices will be reviewed. In the area of glass optics, fabrication of novel microstructured and multi-core fibers and their use in realizing single mode lasers will be summarized. In organic and plastic optics, photorefractive polymers for 3D display applications and nonlinear optical polymers for high speed modulators in RF photon...
متن کاملAll-optical Processes in Integrated Optical Devices Using Materials with Large Third-order Nonlinearities and Gain
متن کامل
Pure χ Third-Harmonic Generation in Noncentrosymmetric Media
Recently, higher-order nonlinear effects have attracted great attention with the development of ultrafast laser technology. Using high peak-power lasers, phase-matched third-harmonic generation (THG) (ω + ω + ω → 3ω) has been demonstrated in solids to directly obtain frequency-tripled output of the fundamental light in a simple way. The beginning of THG experiments using crystals was as early a...
متن کاملAdvanced lasers for photonic device microfabrication
Today’s internet-focused communication industry is driving a powerful transition from slower electronic systems to high-speed all-optical systems. A central effort is the miniaturization and integration of photonic devices into highly functional optical circuits. New processing and packaging technologies are now required that can precisely shape and assemble optical components to sub-wavelength...
متن کامل