Carbon Supported Cu and TiO2 Catalysts Applied for Ozone Decomposition

نویسندگان

  • Katya Milenova
  • Penko Nikolov
  • Irina Stambolova
  • Plamen Nikolov
  • Vladimir Blaskov
چکیده

In this article a comparison was made between Cu and TiO2 supported catalysts on activated carbon for ozone decomposition reaction. The activated carbon support in the case of TiO2/AC sample was prepared by physicochemical pyrolysis and for Cu/AC samples the supports are chemically modified carbons. The prepared catalysts were synthesized by impregnation method. The samples were annealed in two different regimesin air and under vacuum. To examine adsorption efficiency of the samples BET method was used. All investigated catalysts supported on chemically modified carbons have higher specific surface area compared to the specific surface area of TiO2 supported catalysts, varying in the range 590÷620 m/g. The method of synthesis of the precursors had influenced catalytic activity. Keywords—Activated carbon, adsorption, copper, ozone decomposition, TiO2.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Synthesis and Characterization of Carbon Nanotubes Catalyzed by TiO2 Supported Ni, Co and Ni-Co Nanoparticles via CCVD

Monometallic and bimetallic Ni and Co catalytic nanoparticles supported on Titanium dioxide (rutile phase) substrate were prepared by wet impregnation method. These nanoparicles were used as catalysts for synthesis of multiwalled carbon nanotubes (MWCNTs) from acetylene decomposition at 700°C by the catalytic chemical vapor deposition (CCVD) technique. The nanomaterials (catalyst and CNTs) were...

متن کامل

Fischer–Tropsch Synthesis with Cu-Co Nanocatalysts Prepared Using Novel Inorganic Precursor Complex

The structural properties and activities of Cu-Co catalysts used in Fischer-Tropsch synthesis are explored according to their method of preparation. Impregnation, co-precipitation, and a novel method of thermal decomposition were applied to an inorganic precursor complex to generate the Cu-promoted alumina- and silica-supported cobalt catalysts. The precursors and the catalysts obtained by ...

متن کامل

TEM characterisation of novel supported silver and gold nanoparticle catalysts

This project is an extension of TEM work conducted on a previous AINSE funded project AINGRA08066, and aims to use the TEM, STEM/HAADF, EDS and plasmon imaging facilities at ANSTO to structurally characterize novel supported silver nanoparticle catalysts for ozone abatement, and supported gold catalysts for low temperature CO oxidation. The catalysts, fabricated at the University of Auckland, c...

متن کامل

Pt/MOx/SiO2, Pt/MOx/TiO2, and Pt/MOx/Al2O3 Catalysts for

Conventional supported Pt catalysts have often been prepared by loading Pt onto commercial supports, such as SiO2, TiO2, Al2O3, and carbon. These catalysts usually have simple metal-support (i.e., Pt-SiO2) interfaces. To tune the catalytic performance of supported Pt catalysts, it is desirable to modify the metal-support interfaces by incorporating an oxide additive into the catalyst formula. H...

متن کامل

IRON-MODIFIED CARBON-COATED TiO2 FOR ADSORPTION AND DECOMPOSITION OF PHENOL IN WATER

Carbon-coated TiO2 catalysts were found to have high photocatalytic activity for photodecomposition of methylene blue in water, higher than TiO2 without carbon coating [1]. However, these catalysts used for phenol decomposition showed lower activity than TiO2 without carbon coating. Also lower adsorption capacity of phenol on carbon-coated TiO2 catalysts was noted by comparison with adsorption ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2015