Photowritten gratings in ion-exchanged glass waveguides.

UV-exposed Bragg gratings for laser applications in silver-sodium ion-exchanged phosphate glass waveguides.

High reflectivity Bragg gratings have been written by ArF excimer laser through a phase mask into IOG-1 hybrid phosphate glass. After grating exposure, a waveguide was fabricated by silver-sodium ion-exchange. Reflectivities around 80% at a wavelength of ~ 1535 nm were measured from the waveguide for both quasi-TE and -TM polarizations. Waveguide laser operation with the photowritten waveguide ...

Ion-exchanged glass waveguides with low birefringence for a broad range of waveguide widths.

Optical communications networks require integrated photonic components with negligible polarization dependence, which typically means that the waveguides must feature very low birefringence. Recent studies have shown that waveguides with low birefringence can be obtained, e.g., by use of silica-on-silicon waveguides or buried ion-exchanged glass waveguides. However, many integrated photonic cir...

Negligible birefringence in dual-mode ion-exchanged glass waveguide gratings.

Polarization dependence of UV-written Bragg gratings in buried ion-exchanged glass waveguides is investigated. A polarization-dependent shift in Bragg wavelength of less than 0.02 nm is measured, both for the even and the odd modes of a laterally dual-mode waveguide. The measured wavelength shift corresponds to a waveguide birefringence of the order of 10(-5), which is negligible for most appli...

Micro-channels over the glass surface made by interaction of Ar+ laser beam and Ag+/Na+ ion-exchanged glasses

Micro-channels are made over the Ag+/Na+ ion-exchanged soda-lime glass surface by interaction of an intense Ar+ laser beam and the silver ions inside the glass matrix. The Ar+ laser beam reduces the Ag+ ions inside the matrix. The Ag+ atoms aggregate into silver nano-clusters around the interaction area, inside the glass matrix. Aggregation of the silver atoms and the thermal effects of the int...

Studies on Passive and Active Ion-exchanged Glass Waveguides and Devices