Effect of sandblasting on fracture load of titanium ceramic crowns
نویسندگان
چکیده
PURPOSE OF THE STUDY It is difficult to achieve a reliable bond between the titanium and veneering porcelain. The aim of this study was to evaluate the bond strength between titanium ceramic crowns. MATERIALS AND METHODS The surfaces of titanium copings were divided in two groups. Group A sandblasted with 250 um (n = 10) and Group B without sandblasting (n = 10). Low-fusing porcelain was bonded over copings. A universal testing machine was used to determine the fracture load (N) of the crowns. All data were compared using Student's t-test. RESULTS There was a significant difference in fracture toughness between two groups (P = 0.05). The mean value of fracture strength for Group A was 721.66 N and for Group B was 396.39 N. CONCLUSIONS Sandblasting improves the bond strength between titanium, and ceramic, mechanical bonding plays a crucial role in the bonding between titanium and ceramic.
منابع مشابه
CAD/CAM to fabricate ceramic implant abutments and crowns: a preliminary in vitro study.
BACKGROUND This study evaluated the feasibility of fabricating implant abutments and crowns from pre-sintered feldspathic porcelain blocks using the chair-side CAD/CAM, CEREC3D((R)) system. METHODS Thirty-two implant analogues were divided into two groups. In the control group, prefabricated machined anatomical titanium (Ti) abutments were screw-retained to the analogues. In the test group, m...
متن کاملBending moments of zirconia and titanium implant abutments supporting all-ceramic crowns after aging.
OBJECTIVES To test the fracture load and fracture patterns of zirconia abutments restored with all-ceramic crowns after fatigue loading, exhibiting internal and external implant-abutment connections as compared to restored and internally fixed titanium abutments. MATERIALS AND METHODS A master abutment was used for the customization of 5 groups of zirconia abutments to a similar shape (test)....
متن کاملEffect of marginal design on fracture resistance of IPS e.maxall ceramic restorations: Chamfer versus shoulder finish lines
Background and Aim: One of the problems of all ceramic restorations is their risk of fracture due to occlusal loads. The aim of the present study was to compare the effect of two marginal designs (shoulder and chamfer) on the fracture resistance of IPS-emax all ceramic restorations. Materials and Methods: One extracted maxillary first premolar received chamfer 50' marginal preparation (0.8 m...
متن کاملFracture load and survival of anatomically representative monolithic lithium disilicate crowns with reduced tooth preparation and ceramic thickness
PURPOSE To investigate the effect of reducing tooth preparation and ceramic thickness on fracture resistance of lithium disilicate crowns. MATERIALS AND METHODS Specimen preparation included a standard complete crown preparation of a typodont mandibular left first molar with an occlusal reduction of 2 mm, proximal/axial wall reduction of 1.5 mm, and 1.0 mm deep chamfer (Group A). Another typo...
متن کاملEffect of Cyclic Loading on Fracture Strength of Endodontically Treated Teeth Restored with Conventional and Esthetic Posts
INTRODUCTION Esthetic post and core systems were recently introduced. There are few reports regarding their behavior under cyclic loading. OBJECTIVES This study compared the effect of cyclic loading on survival rate, residual strength and mode of fracture of endodontically treated teeth restored with esthetic and direct metallic post systems subjected to mechanical cyclic loading. MATERIALS...
متن کامل