Corrosion Behavior of Copper in Chloride Media

نویسنده

  • M. M. Al-Abdallah
چکیده

The electrochemical behavior of copper in 0.05 M HCl and 0.05 M NaCl carried out at open-circuit potential and at constant anodic potential after one hour has been investigated using electrochemical impedance spectroscopy (EIS) at 20 °C, 40 °C and 60 °C. The formation of copper chloride (CuCl) film does not protect copper from dissolution in the chloride media. The physical properties of the passive film such as, polarization resistance (Rp), capacitance (C), loss factor (%P), Warburg diffusion coefficient (W) and Kugel diffusion constant (k) were obtained from EIS measurements. Also, the radii of the pores formed as a result of anodic polarization have been calculated.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

INVESTIGATING THE CORROSION BEHAVIOR OF NANO STRUCTURED COPPER STRIP PRODUCED BY ACCUMULATIVE ROLL BONDING (ARB) PROCESS IN ACIDIC CHLORIDE ENVIRONMENT

In this research accumulative roll bonding process as sever plastic deformation process was applied up to 8 cycles to produce the ultrafine grain copper. Microstructure of cycle 1, cycle 4 and cycle 8 investigated by TEM images. By analyzing TEM images the grain size measured below 100 nm in cycle 8 and it was with an average grain size of 200 nm. Corrosion resistance of rolled copper stri...

متن کامل

Acetylacetonate Complexes as New Corrosion Inhibitors in Phosphoric Acid Media: Inhibition and Synergism Study

The corrosion inhibition performance of acetylacetonate complexes of zinc(II), manganese(II), cobalt(II) and copper(II) on the mild steel substrate in 1M H3PO4 was studied using DC polarization. It was seen that the mentioned complexes decreased corrosion rate of mild steel in phosphoric acid media due to the adsorption on metal surface. The potential of mild steel shifted toward more active po...

متن کامل

Influence of pH and Chloride Concentration on the Corrosion Behavior of Unalloyed Copper in NaCl Solution: A Comparative Study Between the Micro and Macro Scales

The effects of pH and chloride concentration on the electrochemical corrosion of copper in aqueous sodium chloride (NaCl) media were studied at the micro scale using a microcapillary droplet cell and at the macro scale using a conventional large scale cell. Using an experimental design strategy, electrochemical response surface models of copper versus pH and NaCl concentration were constructed ...

متن کامل

Corrosion Behavior of Polypyrrole/Mesoporous Silica Nanocontainers Coatings on the Mild Steel

The idea of smart corrosion inhibition is basis on either inhibitor consumption where it is needed or reducing harmful matrix interaction with it. In addition, applying corrosion inhibitor in a coating causes many problems such as loss of inhibition capability, coating degradation, or both. A useful technique to overcome th...

متن کامل

Mechanism of copper action on pitting phenomena observed on stainless steels in chloride media

The influence of the addition of copper on the resistance to pitting corrosion of stainless steels has been investigated using different experimental techniques––current transient analysis, polarization curves in acidic media, pitting and repassivation potential measurements, XPS and SEM observations––so that pit initiation, propagation and repassivation could be analysed separately. Copper add...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2009