Conductive Atomic Force Microscopy for Characterization of High-k Dielectrics
نویسندگان
چکیده
The thickness decrease of the SiO2 used as the gate oxide of MOS devices has become one of the main showstoppers of the microelectronic scaling down process, due to a dramatic increase of leakage currents and a decrease in lifetime[1]. The use of an alternative material with a higher dielectric constant (high-K) has been proposed to replace SiO2 as the gate dielectric, because High-K materials will allow to reach the required equivalent oxide thickness (EOT), but with a larger physical oxide thickness, which reduces the leakage current drastically. Most of the knowledge about the electrical behavior of high-k materials has been gained from measurements performed on macroscopic MOS capacitors or transistors[2,3,4] using standard electrical characterization methods at wafer level. This kind of tests, however, provides a spatially averaged information on the electrical properties of the material. On the contrary, Conductive Atomic Force Microscopy (CAFM), as demonstrated for SiO2[5], is able to characterize the gate dielectric at a nanometer scale.
منابع مشابه
A Review on Resistive Switching in High-k Dielectrics: A Nanoscale Point of View Using Conductive Atomic Force Microscope
Metal-Insulator-Metal (MIM) structures have raised as the most promising configuration for next generation information storage, leading to great performance and fabrication-friendly Resistive Random Access Memories (RRAM). In these cells, the memory concept is no more based on the charge storage, but on tuning the electrical resistance of the insulating layer by applying electrical stresses to ...
متن کاملNanoscale Physical Analysis of Localized Breakdown Events in HfO2/SiOX Dielectric Stacks: A Correlation study of STM induced BD with C-AFM and TEM
The study of scanning tunneling microscopy (STM) induced localized dielectric degradation and polarity dependent breakdown (BD) in HfO2/SiOx dielectric stacks is presented in this work, together with a correlated investigation of the BD locations by transmission electron microscopy (TEM). The localized dielectric BD events are also analysed using conductive-atomic force microscopy (C-AFM). The ...
متن کاملApplication of Scanning Electron and Atomic Force Mode Microscopy on inscription from Proto-Elamite period in Tappeh Sofalin
The study of cultural heritage artifacts and the research of a protection and restoration intervention create with - and are often limited to - a complete characterization of their surface. This is not only factual for museum objects, but also for archaeological artifacts, because the object as it was discovered may contain precious unknown information that could be lost by too much aggressive ...
متن کاملNanoscale electrical characterization of HfO2/SiO2 MOS gate stacks with enhanced - CAFM
2.Introduction The replacement in MOS devices of the so far almost perfect SiO2 by another material with a higher dielectric constant (high-k) has been proposed as a solution to the increase in gate current associated to device dimensions shrinking [1]. However, before the effective substitution of SiO2 in commercial IC’s, the electrical properties and reliability of these materials must be wel...
متن کاملHigh Resolution Image with Multi-wall Carbon Nanotube Atomic Force Microscopy Tip (RESEARCH NOTE)
In this paper, a simple and reproducible approach for attaching the multi-wall carbon nanotubes (MWNTs) to the apex of the atomic force microscope probe has been proposed. For this purpose, the dielectrophoresis method was applied due to its simple performance, cheapness and reliability. In this method, various parameters such as voltage, frequency, concentration of carbon nanotubes solution an...
متن کامل