Experimental Determination of Large Strain Localization in Cut Steel Chips

Metal cutting is a severe plastic deformation process involving large strains, high strain rates, and high temperatures. Conventional analysis of the chip formation process is based on bulk material deformation disregarding the inhomogeneous nature of the material microstructure. A series of orthogonal cutting tests of AISI 1045 and 1144 steel were conducted which yielded similar process characteristics and chip formations. With similar shear angles and cut chip thicknesses, shear strains for both chips were found to range from 2.0 up to 2.8. The manganese-sulfide (MnS) precipitate in the 1144 steel has a very distinct and uniform shape which allows for comparison before and after chip formation. From close observations of MnS precipitates in the cut chips it is shown that the conventional approach underestimates plastic strains in metal cutting. Experimental findings revealed local shear strains around a value of 6. These findings and their implications are presented and discussed. Keywords—Machining, metal cutting, microstructure, plastic strains, local strain.