Effect of WC Concentration on Abrasive Wear Properties of the Thermally Sprayed WC -Ni Coatings
نویسنده
چکیده
In this work the effects of WC concentration on abrasive wear behavior by thermally sprayed WC coating was evaluated using three body abrasive wear tester. A different combination of WC and NI coatings were deposited on steel substrates by flame spraying using powder with different WC concentrations (0 %, 12.5 %, 25 %, and 50 %). Flame torch was used for heating and coating of process. Microstructure properties of coated samples were evaluated using optical microscope and wear testing, were performed on the samples.. Experimental results were compared to determine which coating shows the best quality in terms of the wear resistance. It was found that wear resistance is strongly depend on percentage of WC up to a certain level of mixing after that wear resistance will start decreasing.
منابع مشابه
Effect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملThe effects of fuel chemistry and feedstock powder structure on the mechanical and tribological properties of HVOF thermal-sprayed WC–Co coatings with very fine structures
We have deposited a series of WC–Co coatings by the high velocity oxy fuel (HVOF) process, using three different powders, and different spray conditions. The powders are a nanocrystalline (Nanocarb), a near-nanostructured powder (Infralloy) containing a proprietary additive aimed at retarding grain growth, and multimodal (mixed micro and nano) powder (Nanomyte). HVOF spray conditions were stoic...
متن کاملExperimental and Numerical Study of Residual Stress in the WC-12Co HVOF Sprayed Coatings
Thermally sprayed coatings are intrinsically associated with residual stresses in the deposits. These stresses are varied in nature and magnitude, and have a pronounced effect on the mechanical behavior of the system. In the current study, WC-12Co coatings were deposited using HVOF thermal spraying. The sin2ψ method was used to evaluate the through thickness residual stress by means ...
متن کاملEffect of Spray Stand-off on Hardness of Thermally Sprayed Coatings
The mechanical and tribological properties in WC-Co coatings are strongly affected by hardness and elasticity specifications. The results revealed the effect of spraying distance on microhardness and elasticity modulus of coatings. The metallurgical studies have been made on coated samples using optical microscopy, scanning electron microscopy (SEM). Keywords—HVOF, Micro-indentation, Thermal sp...
متن کاملEffect of Spray Stand-off on Elasticity Modulus of Thermally Sprayed Coatings
The mechanical and tribological properties in WC-Co coatings are strongly affected by hardness and elasticity specifications. The results revealed the effect of spraying distance on microhardness and elasticity modulus of coatings. The metallurgical studies have been made on coated samples using optical microscopy, scanning electron microscopy (SEM). Keywords—Elasticity modulus, HVOF, Micro-ind...