Three-dimensional analysis of coalesced bainite using FIB tomography
نویسندگان
چکیده
A coarse grained constituent recently discovered in high strength steel weld metals – Coalesced Bainite – was investigated with a serial section procedure for three-dimensional (3D) analysis using Focused Ion Beam (FIB) milling. Image planes of a coalesced bainite grain, 0.4 μm apart were acquired using the FIB. The data collected was then used to create a 3D model of the coalesced bainite grain. The reconstruction, revealed the grain was large chunky in all three dimensions which was greater than 20 μm in length. Correlations were made between the 3D reconstruction and micrographs of the same coalesced bainite grain recorded using Field Emission Gun Scanning Electron Microscopy and Light Optical Microscopy to allow an understanding in 3D when making future interpretations using the latter characterisation techniques. Materials Characterisation 59 (2008) 877-882
منابع مشابه
Electron backscattering diffraction study of coalesced bainite in high strength steel weld metals
Coalesced bainite is a coarse constituent recently found to develop along with the classical martensite, lower and upper bainite in steel weld metals. Its crystallography has been characterised using electron backscattering diffraction in combination with field emission gun scanning electron microscopy. It is confirmed that coalesced bainite grains are crystallographically homogeneous but do co...
متن کاملMicrostructure characterisation of a high strength steel weld metal containing the novel constituent coalesced bainite
An experimental high strength steel weld metal containing 7 wt. % nickel and 2 wt. % manganese was found to have a complex microstructure. Employing high resolution characterisation techniques the microstructure consisted primarily of a mixture of martensite, upper bainite and a novel constituent with large grain size that contained plate-like precipitates. This constituent was characterised to...
متن کاملUnderstanding Mechanical Properties of Novel High Strength Steel Weld Metals Through High-Resolution Microstructural Investigations
Shielded metal arc welding and submerged arc welding were used to prepare experimental weld metals with variations in nickel, manganese and carbon contents. The weld metals contained Ni between 6.6 and 10.5 wt. %, Mn between 0.5 and 2.0 wt. % while carbon was varied between 0.03 and 0.11 wt. %. Mechanical properties were found to be sensitive to alloying content. However once the optimum level ...
متن کاملInfluence of carbon, manganese and nickel on microstructure and properties of strong steel weld metals Part 2 – Impact toughness gain resulting from manganese reductions
Two experimental high strength steel weld metals were produced with 7 wt-% nickel and either 2 or 0.5 wt-% manganese. Neural network predictions that it is advantageous to reduce the manganese concentration in high nickel alloys have been confirmed, with impact energy increasing from 32 to 113 J at –40uC. High resolution microstructural investigations showed that both weld metals contained main...
متن کاملInfluence of C, Mn and Ni Contents on Microstructure and Properties of Strong Steel Weld Metals — Part II. Impact Toughness Gain from Manganese Reductions
Two experimental high strength steel weld metals were produced with 7 wt. % nickel and manganese at 2 or 0.5 wt. %. Neural network predictions that Mn reductions increase toughness were confirmed with impact energy increasing from 32 to 113 J at –40 °C. High resolution microstructural investigations showed that both weld metals contained mainly martensite at interdendritic regions and predomina...