Electrophoretic deposition of ZnO nanoparticles, from micropatterns to substrate coverage.

نویسندگان

  • P Lommens
  • D Van Thourhout
  • P F Smet
  • D Poelman
  • Z Hens
چکیده

We report on an electrophoretic deposition (EPD) method that is suited for the preparation of both ZnO thin films and micropatterns. By applying small DC voltages between a Cu electrode and a conductive Si substrate, submersed in a suspension of ZnO quantum dots, we can cover entire substrates with ZnO layers of a tuneable thickness ranging from a few monolayers to 200 nm. The deposition occurs selectively at the cathode, which indicates that the ZnO particles have a positive charge. Atomic force microscopy was used to study the influence of the deposition voltage, time, and the quantum dot concentration on the final layer thickness. By using lithographically patterned Si substrates, the same technique enables the formation of ZnO micropatterns of variable thickness with dimensions down to 5 µm. This is done by depositing a ZnO layer on a Si substrate that is covered with a patterned, developed photoresist. After EPD, the resist is removed by submersing the substrate in the appropriate solvent without damaging the ZnO deposit. This illustrates the robustness of the layers obtained by EPD.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Multi-step Electrophoretic Deposition of α-Al2O3 Nanoparticles on Carbon Substrate (TECHNICAL NOTE)

in the present study, electrophoretic deposition (EPD) was used to obtain dense and crack-free layers of Al2O3 on carbon substrate. Microstructural study of the obtained layers by scanning electron (SEM) and optical microscopy (OM) approved that crack-free layers can be obtained by EPD technique. According to obtained results, isopropanol is a suitable media to obtian compact layers which is at...

متن کامل

Titanium Oxide (TiO2) Coatings on NiTi Shape Memory Substrate Using Electrophoretic Deposition Process

The aim of the present research is to convert bioinert surface of NiTi to bioactive and biocompatible surface. In order to develop a bioactive and corrosion resistant film on NiTi, electrophoretic deposition process was done and TiO2 particles were deposited on the NiTi surface. Suspensions including TiO2 particles were prepared using a mixture of acetone and n-butanol (0%, 30%, 60%, 80% and 10...

متن کامل

Electrophoretic deposition and corrosion behavior study of aluminum coating on AZ91D substrate

Aluminum coating was prepared on AZ91D magnesium alloy substrate using the electrophoretic deposition (EPD) method in absolute ethanol solvent. In order to determine the optimal concentration of AlCl3.6H2O additive, the zeta potential and size of particles in the suspension were measured in the presence of different concentrations of AlCl3.6H2O. The results showed that an appropriate coating is...

متن کامل

Affectability of ceramic nanoparticles of different compound from surface characteristics in AC electrophoretic deposition

Surface characteristic of particles is one of the main parameters controlling the properties of deposited layer in electrophoretic deposition. To modify the surface characteristic of particles, one of the methods is the addition of additives to the suspensions of powder-solvent. There are many reports dealing with the effect of surface characteristics of particles on uniformity and pattern of d...

متن کامل

ELECTROPHORETIC DEPOSITION OF TIO2-MULTI-WALLED CARBON NANOTUBE COMPOSITE COATINGS: MORPHOLOGICAL STUDY

A homogenous TiO2 / multi-walled carbon nanotubes(MWCNTs) composite film were prepared by electrophoretic co-deposition from organic suspension on a stainless steel substrate.  In this study, MWCNTs was incorporated to the coating because of their long structure and their capability to be functionalized by different inorganic groups on the surface. FTIR spectroscopy showed the existence of...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Nanotechnology

دوره 19 24  شماره 

صفحات  -

تاریخ انتشار 2008