An in vitro evaluation of the effect of sandblasting and laser surface treatment on the shear bond strength of a composite resin to the facial surface of primary anterior stainless steel crowns
نویسندگان
چکیده
OBJECTIVES The present study was conducted to evaluate the optimal method of enhancing the bond strength of a composite resin to the facial surface of the primary anterior stainless steel crowns using various surface treatments namely Nd: YAG laser surface treatment, sandblasting , alloy primer application and no surface treatment. STUDY DESIGN The study sample consisted of 60 primary anterior stainless steel crowns (UnitekTM size R 4), with 15 samples randomly divided into the 4 study groups, embedded in acrylic blocks. The facial surface of these surface treated crowns was utilized as the bonding surface to which 2.5mm diameter composite resin cylinders were bonded for the evaluation of the shear bond strength. Shear bond strength measurements were made using a universal testing machine utilizing a shearing blade (jig).The mode of failure at composite-metal interface was determined using a Stereomicroscope at 10 X magnification. RESULTS The mean bond strength values obtained for surface treatment of Nd: YAG laser surface treated, Sandblasting ,Alloy Primer and No surface treatments were 17.01±.92 , 13.18 ± .73, 7.46 ± .70 and 7.33 ± .77 MPa respectively. The obtained bond strength values were subjected to a one way ANOVA and a Scheffe's post-hoc comparison test. The results of the present study indicated that Laser surface treatment of the facial surface of the crowns enhanced the bond strength of the composite resin significantly compared to the other groups. CONCLUSIONS Nd: YAG laser surface treatment produced an excellent surface roughness and obtained the highest shear bond strength values suggestive for recommendation as an optimal surface treatment to be used to enhance the resin-metal bond at the interface of the composite resin and the facial surface of primary anterior stainless steel crowns for the purpose of chairside veneering. Key words:Nd: YAG laser treatment, Sandblasting, Primary anterior stainless steel crown, Chairside veneering, Enhancing Resin-Metal Bond, Early childhood caries, Shear bond strength (SBS).
منابع مشابه
In vitro evaluation of the effect of different surface treatments and bonding systems on shear bond strength of composite veneer to Stainless Steel Crown
Abstract Background and aim: Using Stainless Steel Crowns (SSC) for Early Childhood Caries usually causes an unpleasant condition in the aesthetic of the patients. The aim of this study was to evaluate the effect of different surface treatments and bonding systems on shear bond strength of composite veneer to Stainless Steel Crown. Materials and Methods: In this in vitro study, 120 SSC were ...
متن کاملIn Vitro Effects of Different Surface Preparation Techniques on Shear Bond Strength of Direct to Indirect Composite Resin
Objective: Repair of an indirect restoration is usually preferred over its replacement. This study aimed to evaluate the effect of silane in different surface preparation techniques on the bond strength of direct to indirect composite resin. Methods: For this in vitro experimental study, 48 indirect composite cubes were fabricated, divided into 4 groups of 12 and subjected to the following ...
متن کاملEffect of Er: YAG laser, diamond bur and sandblasting on the microtensile bond strength of the composite to noncarious cervical lesions
Background and Aims: Restoration of non-carious cervical lesions (NCCLs) is challenging due to the difficulty of adhesion of dental tissues. The aim of this study was to investigate the effects of three methods of surface treatments using diamond bur, Er: YAG laser and sandblasting on the microtensile bond strength of resin composite to the noncarious dentin in cervical lesions. Materials and ...
متن کاملEffect of Type of Surface Treatment and Adhesive System on Shear Bond Strength of Composite Resin to a Non-Precious Metal Alloy
Background and Aim: Fractured metal-ceramic restorations may be repaired with composite in some cases to postpone the fabrication of a new restoration. Knowledge about the bond strength can help predict the success rate of this treatment modality. The aim of this study was to assess the effect of two types of mechanical surface treatment of metal along with the use of different adhesive systems...
متن کاملIn-vitro Comparison of the Impact of Four Types of Resin Composite on the Repaired Bond Strength and Surface Roughness After Sandblasting
Abstract Background and Aim: One of the major problems with resin composite restorations is the weakness of bonding between the new and aged composites. Since appropriate micromechanical retention is necessary for the repair of aged resin composite restorations, the level of surface roughness after sandblasting can be influential in this regard. Considering the diverse composition of avail...
متن کامل