Current Oscillations in Epoxy-coated Steel at Anodic Polarization
نویسنده
چکیده
The current oscillatory behavior of epoxy-coated low carbon steel at anodic polarization was investigated in 3,5 % and 0,5 % solutions of NaCl. It was established, that the coated steel may show current oscillations at potentiostatic anodic polarization. The oscillations are of different type, period and amplitude and are more clearly expressed in 0,5 % solution. The presented results might be used in the field of electrochemistry, electronics and electrical engineering as well as in the field of oscillatory systems study.
منابع مشابه
09207 - Corrosion of Epoxy- and Polymer/zinc- Coated Rebar in Simulated Concrete Pore Solution
This work is a preliminary examination of mechanistic issues on the comparative corrosion performance of regular epoxy-coated rebar (ECR) and dual polymer-zinc coated reinforcement (DCR) in simulated concrete pore solution with and without chloride ions, at polarizations from +100 mV to -1000 mV in the saturated calomel electrode (SCE) scale and exposure periods of 1 month or longer. Both mater...
متن کاملDETERIORATION OF PITTING CORROSION OF 316 STAINLESS STEEL BY SENSITIZATION HEAT TREATMENT
In this research pitting Corrosion of a sensitized 316 stainless steel was investigated employing potentiodynamic, potentiostatic techniques. Sensitization process was carried out on as-received alloy by submitting the specimen in electric furnace set at 650°Cfor five hours and then the specimen was quenched 25°C water. Potentiodynamic polarization of as received and sensitized specimens in 1M ...
متن کاملCATHODIC PROTECTION OF STEEL REINFORCED CONCRETE BY CONDUCTIVE EPOXY PAINTS IN MARINE ENVIRONMENTS
Anodes are critical component of cathodic protection systems. As part of this effort, three different anodes were tested in a cathodic protection system that was designed and constructed to prevent further corrosion of reinforced concrete. This anodic system includes an electrically conductive coating composition applied in fluid form over an outer surface of the concrete mix. The composition f...
متن کاملEffect of current density on the microstructure and polarization resistance of Ni-P-TiO2-ZrO2 composite coating
Composite coatings with nickel matrix and ceramic reinforcement particles have high ability to improve surface properties, such as good corrosion and abrasion resistance. In this study, Ni-P composite coating was coated with ZrO2 and TiO2 ceramic particles on the AISI 316 steel substrate through direct current plating method. The effect of the current densities of 20, 30, 40 and 50 mA/cm2 on th...
متن کاملEnhanced Anti-corrosive Properties of Electrosynthesized Polyaniline/zeolite Nanocomposite Coatings on Steel
The preparation of polyaniline/zeolite nanocomposite coating on 304 stainless steel (304 SS) surface has studied via the galvanostatic method. The electro-generated coating was characterized by Fourier transform infrared spectroscopy (FT-IR), UV-visible absorption spectroscopy, X-ray diffraction (XRD) patterns and scanning electron microscopy (SEM). The anticorrosion property of polyaniline/zeo...
متن کامل