Solid-phase electrochemical reduction of graphene oxide films in alkaline solution
نویسندگان
چکیده
Graphene oxide (GO) film was evaporated onto graphite and used as an electrode to produce electrochemically reduced graphene oxide (ERGO) films by electrochemical reduction in 6 M KOH solution through voltammetric cycling. Fourier transformed infrared and Raman spectroscopy confirmed the presence of ERGO. Electrochemical impedance spectroscopy characterization of ERGO and GO films in ferrocyanide/ferricyanide redox couple with 0.1 M KCl supporting electrolyte gave results that are in accordance with previous reports. Based on the EIS results, ERGO shows higher capacitance and lower charge transfer resistance compared to GO.
منابع مشابه
Comparative studies on single-layer reduced graphene oxide films obtained by electrochemical reduction and hydrazine vapor reduction
The comparison between two kinds of single-layer reduced graphene oxide (rGO) sheets, obtained by reduction of graphene oxide (GO) with the electrochemical method and hydrazine vapor reduction, referred to as E-rGO and C-rGO, respectively, is systematically studied. Although there is no morphology difference between the E-rGO and C-rGO films adsorbed on solid substrates observed by AFM, the red...
متن کاملFabrication of Graphene Oxide Thin Films on Transparent Substrate via a Low-Voltage Electrodeposion Technique
Graphene oxide (GO) thin films were simply deposited on fluorine doped tin oxide (FTO) substrate via a low-voltage electrodeposition. The GO and GO thin films were characterized by Zeta Potential, X-ray diffraction, Ultraviolet-Visible spectroscopy, atomic force microscopy, Fourier transform infrared spectroscopy, field emission scanning electron microscopy and energy dispersive X-ray spectrosc...
متن کاملSynthesis and characterization of porous zinc oxide nano-flakes film in alkaline media
In this study, porous zinc oxide nano-flakes were successfully synthesized by anodization method on zinc substrate in a 0.025 M NaOH and 0.05 M NH4Cl solution with the voltage of 10 V at room temperature. The field emission scanning electron microscopy’s (FESEM) images show the structural evolution during 90 min of the anodization process. They also demonstrate the dependency of growth of ZnO f...
متن کاملElectrodeposition of platinum nanoparticles on reduced graphene oxide as an efficient catalyst for oxygen reduction reaction
Reduced graphene oxide film was synthesized on a glassy carbon electrode by electro reduction of graphene oxide powders in aqueous solution. Then platinum nano particles were deposited on reduced graphene oxide film that was deposited on the glassy carbon electrode via electro reduction of platinum salt. The Physical morphology of the platinum on reduced graphene oxide film was evaluated by sca...
متن کاملCapacitance Properties of Electrochemically Synthesised Polybithiophene-Graphene Exfoliated Composite Films
The graphene (GR) has attracted intensive interest due to its two-dimensional and unique physical properties. In the present study, the graphene sheets were synthesized by electrochemical exfoliation of graphite in sulfuric acid solution. The polybithiophene-graphene (PbTh-GR) composite films deposited onto indium tin oxide substrate (ITO/PbTh-GR) have been prepared by the incorporation of ...