Dispersion of alkyl-chain-functionalized reduced graphene oxide sheets in nonpolar solvents.

نویسندگان

  • Jean-Philippe Tessonnier
  • Mark A Barteau
چکیده

Alkyl chains were grafted onto reduced graphene oxide sheets to allow their dispersion in toluene, a common and representative nonpolar solvent. The grafting occurred on a variety of oxygen-containing functionalities already present on reduced graphene oxide, such as hydroxyl and epoxide groups. The structure and the defect density of the sheets were not significantly altered during the synthesis. When dispersed in water-toluene mixtures, phase transfer from the aqueous to the organic phase was observed upon grafting. In addition, the dry powder obtained readily disperses in common organic solvents without the assistance of any sonication treatment.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Chemical and Structural Characterization of Intercalated Graphene Oxide and Their Dispersibility in Organic Solvents

Graphene, a two-dimensional honeycomb lattice of sp 2 hybrid carbon, exhibit combination of unique characteristics such as high thermal and electrical conductivity, excellent mechanical strength and very high specific surface area, which promises their great potential for various applications including nanoelectronics, catalysis, sensors, energy storage devices, polymer composites, lubricants a...

متن کامل

Noncovalent functionalization of graphene with end-functional polymers†

Stable dispersion of reduced graphene in various organic solvents was achieved via noncovalent functionalization with amine-terminated polymers. An aqueous dispersion of reduced graphene was prepared by chemical reduction of graphene oxide in aqueous media and was vacuum filtered to generate reduced graphene sheets. Good solvents and nonsolvents for the dried reduced graphene were evaluated usi...

متن کامل

Studying the Corrosion Protection Behavior of an Epoxy Composite Coating Reinforced with Functionalized Graphene Oxide by Second and Fourth Generations of Poly(amidoamine) Dendrimers (GO-PAMAM-2, 4)

In this research, graphene oxide (GO) nanoparticles were modified by second and fourth generations of poly(amidoamine) dendrimers in order to improve the particle dispersion quality in the epoxy matrix and therefore its barrier anti-corrosion performance. Confirmation on the GO surface modification by Polyamidoamine generation 2 (PAMAM2) and polyamidoamin generation 4 (PAMAM4) was carried o...

متن کامل

Purified dispersions of graphene in a nonpolar solvent via solvothermal reduction of graphene oxide.

It is demonstrated that oxidative debris can be separated and largely removed during the surfactant assisted phase transfer of graphene oxide from a water/ethanol mixture to dichlorobenzene. The new procedure described provides a facile method to obtain monolayer dispersed graphene sheets in a nonpolar solvent via solvothermal reduction of graphene oxide accompanied by an effective purification...

متن کامل

High-quality reduced graphene oxide-nanocrystalline platinum hybrid materials prepared by simultaneous co-reduction of graphene oxide and chloroplatinic acid

Reduced graphene oxide-nanocrystalline platinum (RGO-Pt) hybrid materials were synthesized by simultaneous co-reduction of graphene oxide (GO) and chloroplatinic acid with sodium citrate in water at 80°C, of pH 7 and 10. The resultant RGO-Pt hybrid materials were characterized using transmission electron microscopy (TEM), powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), F...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:
  • Langmuir : the ACS journal of surfaces and colloids

دوره 28 16  شماره 

صفحات  -

تاریخ انتشار 2012