Effect of Calcination on the Sintering Behaviour of Hydroxyapatite
نویسنده
چکیده
*Centre for Advance Manufacturing & Materials Processing, Department of Mechanical Engineering, Faculty of Engineering, University of Malaya 50603, Kuala Lumpur, Malaysia **Division of Neurosurgery, Faculty of Medicine, University of Malaya, Kuala Lumpur 50603, Malaysia ***Ceramics Technology Group, SIRIM Berhad, Shah Alam 40911, Malaysia ****Department of Electronics and Communication, College of Engineering, Universiti Tenaga Nasional, Km-7, Jalan Ikram-UNITEN, 43009 Kajang, Selangor, Malaysia
منابع مشابه
Effect of Sintering Temperature on Some Physical And Mechanical Properties of Fabricated Hydroxyapatite Used For Hard Tissue Healing
This work focuses on studying the role of drying and calcination on stiochiometry and crystallinity of deposited HA. Also, studying the effect of sintering temperature on phases generated, physical and mechanical properties of sintered HA powder compact at a range of (800-1200) ̊ C. Both Ca/P ratio and crystallinity were increased after calcination, where the Ca/P ratio raised from 1.7 to 1.9 an...
متن کاملEffect of Calcination Kinetics and Microwave Sintering Parameters on Dielectric and Peizo-Electric Properties of(K0.5Na0.5) NBO3 Ceramics
An efficient solid-state approach was established to synthesize (K0.5Na0.5) NbO3 ceramics using calcination kinetics and microwave assisted sintering. Milling of carbonate and oxide raw materials were carried out for 15h to obtain homogeneous nano particles. The crystallite size of 5.30 nm was obtained for the KNN system after calcination through optimized parameters and observed to be stoichio...
متن کاملTHE EFFECT OF RAW MATERIALS CONCENTRATION ON HYDROXYAPATITE POWDER CHARACTERISTICS AND SINTERING BEHAVLOR
Ultrafine hydroxyapatite (HAp) powders with crystallite size in the range of 10-90 nm were synthesized by chemical precipitation process using Ca(OH)2 and H3PO4 solutions as starting materials. Molar ratio of Ca/P=1.68 was kept constant throughout the process and alkaline condition for the reaction was maintained using ammonium hydroxide. The role of raw material concentration on HAp crystallit...
متن کاملFabrication and characterization of highly crystalline Hydroxyapatite used for bone joining, replacement and reconstruction
This work focuses on studying the effect of sintering temperature ,pressing pressure and sintering time (soaking time) on phases generated, porosity and fracture strength of sintered HA powder compact at a range of (800-1200) ̊C , (38.378-153.513)Mpa and (1-5)hr respectively, and evaluation of sintered HA powder compact in synthetic body fluids(SBF), to indicate the biological bioactivity . Both...
متن کاملShynthesis and Characterizations of Calcium Hydroxyapatite Derived from Crabs Shells (Portunus pelagicus) and Its Potency in Safeguard against to Dental Demineralizations
Crab's shells of Portunus pelagicus species were used as raw materials for synthesis of hydroxyapatite were used for protection against demineralization of teeth. Calcination was conducted to crab's shells of Portunus pelagicus at temperature of 1000°C for 5 hours. The results of calcination was reacted with (NH4)2HPO4, then dried at 110°C for 5 hours. Sintering was conducted to results of prec...