Niobium Wires as Space Holder and Sintering Aid for Porous NiTi
نویسنده
چکیده
When NiTi powder compacts containing Nb wires are heated above 1 170 8C, each Nb wire reacts with adjacent NiTi powders to form a eutectic liquid which wicks into the space between the remaining NiTi powders. This creates a macropore at the location of the Nb wire while eliminating the microporosity between NiTi powders which is filled with a NiTi/Nb eutectic phase after solidification. This novel method produces – in a single step and without applied pressure – a dense NiTi matrix with elongated pores suitable for shape memory or superelastic applications such as bone implants, dampeners and actuators.
منابع مشابه
Synthesis of Porous Nanostructure NiTi Implant and Measurement of Thermomechanical Properties
Objective(s): NiTi is known as the most important material for manufacturing implants and medical devises duo to its shape memory and superelasticity properties, high energy damping, and high corrosion resistance. Methods: In this project, the possibility of producing nanostructured NiTi implant with high porosity was investigated. For reaching to the nan...
متن کاملMicrostructure, mechanical properties and superelasticity of biomedical porous NiTi alloy prepared by microwave sintering.
Porous NiTi alloys were prepared by microwave sintering using ammonium hydrogen carbonate (NH4HCO3) as the space holder agent to adjust the porosity in the range of 22-62%. The effects of porosities on the microstructure, hardness, compressive strength, bending strength, elastic modulus, phase transformation temperature and superelasticity of the porous NiTi alloys were investigated. The result...
متن کاملBiomimetic modification of porous TiNbZr alloy scaffold for bone tissue engineering.
Porous titanium (Ti) and Ti alloys are important scaffold materials for bone tissue engineering. In the present study, a new type of porous Ti alloy scaffold with biocompatible alloying elements, that is, niobium (Nb) and zirconium (Zr), was prepared by a space-holder sintering method. This porous TiNbZr scaffold with a porosity of 69% exhibits a mechanical strength of 67 MPa and an elastic mod...
متن کاملShape-memory NiTi–Nb foams
A new powder metallurgy technique for creating porous NiTi is demonstrated, combining liquid phase sintering of prealloyed NiTi powders by Nb additions and pore creation by NaCl space-holders. The resulting foams exhibit well-densified NiTi–Nb walls surrounding interconnected pores created by the space-holder, with controlled fraction, size, and shape. Only small amounts of Nb (3 at.%) are need...
متن کاملPorous NiTi alloy prepared from elemental powder sintering
An elemental powder sintering (EPS) technique has been developed for the synthesis of porous NiTi alloy, in which Ni and Ti powders are used as the reactants and TiH2 powder is added as a pore-forming agent and active agent. Effects of various experimental parameters (sintering temperature, sintering time, and TiH2 content) on the porosity, pore size and pore distribution as well as phase compo...
متن کامل