Fly Ash-Based Geopolymer Mortar Incorporating Bottom Ash
نویسنده
چکیده
This paper presents the results of study on effect of various parameters on mechanical properties of fly ash-based geopolymer mortar with bottom ash as partial or full replacement for sand. Compressive strength of samples with 10% bottom ash (BA) was comparable to those with only sand. Further increase in bottom ash content decreased the compressive strength. However, the reverse tendency occurred after exposing the samples to 1000C for 24 hours.
منابع مشابه
Study of Fly Ash Geopolymer Based Composites with Polyester Waste Addition
In the present work, fly ash geopolymer based composites including polyester (PES) waste were studied. Specimens of three compositions were prepared: (a) fly ash geopolymer with 5% PES waste; (b) fly ash geopolymer mortar with 5% PES waste; (c) fly ash geopolymer mortar with 6.25% PES waste. Compressive and bending strength measurements, water absorption test and determination of thermal conduc...
متن کاملMechanical Properties and Microstructure of Class C Fly Ash-Based Geopolymer Paste and Mortar
This paper presents workability, compressive strength and microstructure for geopolymer pastes and mortars made of class C fly ash at mass ratios of water-to-fly ash from 0.30 to 0.35. Fluidity was in the range of 145-173 mm for pastes and 131-136 mm for mortars. The highest strengths of paste and mortar were 58 MPa and 85 MPa when they were cured at 70 °C for 24 h. In XRD patterns, unreacted q...
متن کاملEffect Of Na2o/Al2o3, Sio2/Al2o3 And W/B Ratio On Setting Time And Workability Of Flyash Based Geopolymer
The objectives of the present research is to appreciate the effect of synthesizing parameters on setting time and workability of Fly ash based geopolymer paste . Locally available low calcium fly ash from a thermal power plant located near Kolkata, India, was used . Fly ash used are lignite coal based and falls under class F category. The broad areas of present research include: Manufacturing o...
متن کاملProduction geopolymer materials by coal fly ash
Coal ash is the main waste from power plant. It is estimated that the consumption of the coal for power plant will increase to 240 million tons each year and the coal ash wastes will produce more than 2 million tons per year. Although the utilization of coal fly ash can be reached 74.1%, large amount of coal fly ash and bottom ash still cannot be utilized. The purpose of this research is to dev...
متن کاملInfluence of Curing on the Strength Development of Calcium-Containing Geopolymer Mortar
This paper investigated the curing effects on the mechanical properties of calcium-containing geopolymer mortar. Three precursors are used: Class C fly ash, Class F fly ash plus calcium hydroxide and Class F fly ash plus slag. Curing conditions included: (1) standard curing at 20 ± 3 °C and RH 95% (C); (2) steam curing at 60 °C for 24 h (S); (3) steam curing at 60 °C for 6 h (S6); and (4) oven ...