Combustion and Ball Milled Synthesis of Rare Earth Nano-Sized Ceria Powder
نویسندگان
چکیده
This paper reports a study on nanocrystalline ceria powder prepared by high energy ball-milling and combustion synthesis methods. The combustion synthesis was carried out using ceric ammonium nitrate as oxidizer and citric acid, glycine or citric acid plus glycine as fuel. The minimum crystallite size of ceria powder is obtained by combustion synthesis of ceric ammonium nitrate and citric acid. The ceria powder produced by combustion synthesis of ceric ammonium nitrate and citric acid and glycine has less agglomeration of particles than other techniques.
منابع مشابه
Effect of Synthesis Routes on Microstructure of Nanocrystalline Cerium Oxide Powder
The effect of different processing routes on the microstructure of nanocrystalline ceria powder has been investigated. The nanocrystalline ceria is produced by solid state high energy ball milling (HEBM) and liquid state solution combustion synthesis (SCS) method. The liquid state route consists of a high temperature combustion reaction to form ceria from an aqueous solution of cerium ammonium ...
متن کاملMicrowave induced combustion Synthesis of Nano- Codoped Ceria and their electrical properties
In this work, Ce0.75Gd0.1Ca0.15O1.8 nanopowders are successfully synthesized by a Glycine-nitrate combustionprocess under the microwave irradiation. Then calcination was carried out at 700 °C. Calcined powdersidentified by room temperature X-ray diffraction were single phase and had a crystallite size between 16 to 24nm (based on Schererr formula). Scanning electron microscopy (SEM) was employe...
متن کاملSynthesis of Nano-Ca doped Ceria by combustion method and investigating of effective factors on process
A Synthesis of doped ceria by combustion method is performed. Two types of fuel such asurea and glycine is used to investigate the effect of fuel reactivity and reaction rate on themorphology of the resulted powders. Thermo gravimetric analysis is carried out by (TG/DTA,Rigaku Thermalplus TG 8120) to study the exo–endo temperature of as-received powder. Thecrystalline phases are identified by X...
متن کاملEffect of processing parameters on the mechano-chemical synthesis of nano crystalline Mo-Cu/Al2O3 composite
In this study, molybdenum-copper/alumina nano composite was synthesized with mechano-chemical method using high energy planetary ball milling. The molybdenum oxide, copper oxide and aluminum powder were used as starting materials and reaction appeared to occur through a rapid combustion reaction process. The evaluation of powder particles after different milling times was studied by X-ray diffr...
متن کاملTHE EFFECT OF MILLING CONDITIONS ON THE MECHANICAL ALLOYING AND COMBUSTION SYNTHESIS OF TIO2-AI-C POWDER MIXTURE
A mixture of Tio2+Al+C powders was mechanically activated using a planetary ball mill under different milling conditions wherein the milled powders were further subjected to combustion synthesis to produce TiC+Al2O3 composite. The mechanically alloyed powders were characterized by X-Ray diffraction analysis and TEM investigations. XRD analysis of milled powder mixture showed no significant reac...
متن کامل