Selective Formation of Light Olefins from CO+H2 Over Silica Supported Co/CeO2 Prepared by Fusion Method: Preparation, Characterization and Operational Conditions Effects

نویسندگان

  • A. Beigbabaei
  • A. Youssefi
چکیده

The catalyst containing 80%Co/20%Ce/15wt%SiO2 was prepared using fusion procedure and studied for the conversion of synthesis gas to light olefins. The effect of a range of operating variables such as the pressure, temperature and H2/CO molar feed ratio on the catalytic performance of fused catalyst was investigated. It was found that the best operating conditions are H2/CO=2/1, T=350 ̊C and P=2 bar. The results are interpreted in terms of the structure of active catalyst. Characterization of both precursor and calcined catalysts was carried out using Powder X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and BET surface area measurements.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

KCl Promoted Cobalt-iron Nanocatalysts Supported on Silica: Catalytic Performance and Characterization in Fischer-Tropsch Synthesis

The SiO2 supported cobalt-iron nano catalysts were prepared by the sol-gel method. This research investigated the effects of (Co/Fe) wt.%, different Co/Fe ratio at different temperature and loading of KCl wt.% for Fisher-Tropsch synthesis (FTS). The results were showed that the catalyst containing 50 wt.% (Co/Fe)/SiO2 (Co/Fe ratio is 70/30) which promoted with 0.6 wt.% KCl is an optimal nano ca...

متن کامل

Optimizing the Preparation Conditions of Silica Supported Fe-Co-Ce Ternary Catalyst for the Fixed-bed Fischer-Tropsch Synthesis: Taguchi Experimental Design Approach

Using wet impregnation method, a novel ternary system of silica supported Fe-Co-Ce catalyst was prepared. Preparation conditions such as impregnation time and temperature, drying time and temperature, were optimized by the L9 Taguchi experimental design to achieve a light olefin selective catalyst with maximum CO conversion in a fixed bed micro-reactor. It was found that the best conditions to ...

متن کامل

Preparation and Characterization of CoMn/TiO2 Catalysts for Production of Light Olefins

A series of x(Co, Mn)/TiO2 catalysts (x=2–12wt.%) containing 25%Co and 75%Mn were prepared by the co-impregnation method. All prepared catalysts have been tested in Fischer-Tropsch synthesis for production of C2-C4 olefins. It was found that the catalyst containing 8wt.%(Co,Mn)/TiO2 is an optimal catalyst for production of C...

متن کامل

Fischer–Tropsch Synthesis with Cu-Co Nanocatalysts Prepared Using Novel Inorganic Precursor Complex

The structural properties and activities of Cu-Co catalysts used in Fischer-Tropsch synthesis are explored according to their method of preparation. Impregnation, co-precipitation, and a novel method of thermal decomposition were applied to an inorganic precursor complex to generate the Cu-promoted alumina- and silica-supported cobalt catalysts. The precursors and the catalysts obtained by ...

متن کامل

A review of Fischer-Tropsch synthesis on the cobalt based catalysts

Fischer-Tropsch synthesis is a promising route for production of light olefins via CO hydrogenation over transition metals. Co is one of the most active metals for Fischer-Tropsch synthesis. Some different variables such as preparation parameters and operational factors can strongly affect the selectivity of Fischer-Tropsch synthesis toward the special products. In the case of preparat...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010