WIDE – RANGING INFLUENCE OF MISCHMETAL ON PROPERTIES OF G17CrMo5-5 CAST STEEL
ثبت نشده
چکیده
J. Kasińska, Faculty of Mechatronics and Machine Design, Kielce University of Technology, Kielce, Poland This paper presents influence of rare earth metals (REM) on the mechanical properties, microstructure and morphology of non metallic inclusions as well as the cracking mechanism of G17CrMo5-5 high temperature cast steel. The research has been performed on successive industrial melts. It was found that non metallic inclusions the cracking mechanism of Charpy specimens and the impact strength were all changed. The following properties were tested: mechanical properties (Rm, Re), plastic properties (A, Z), impact strength (SCI) and the KJC stress intensity factor.
منابع مشابه
MODIFICATION INFLUENCE OF MISCHMETAL ON FRACTOGRAPHY FRACTURE OF G17CrMo5-5 CAST STEEL SAMPLES AFTER THE THREE-POINT BENDING TEST
J. Kasińska, Faculty of Mechatronics and Machine Design, Kielce University of Technology, Kielce, Poland The article presents the analysis of fracture surfaces after the three-point bending test at a temperature range from + 20 °C to 80 °C. The author shows a beneficial effect of mischmetal on the cracking mechanism and on the character of fractures. It has been shown that the width of the duct...
متن کاملInfluence of Cu and Ni on the Microstructure and Mechanical Properties of an HSLA Steel
In this research the role of alloying elements on the microstructure and mechanical properties of an as cast and hot rolled high strength low alloy (HSLA) steel was studied. Different compositions with different amount of copper in the presence of nickel, hot rolled and quenched in oil. Tensile test, hardness test, scanning electron microscope (SEM) and optical microscope (OM) were used to eval...
متن کاملEFFECTS OF MO ADDITION ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF CAST MICROALLOYED STEEL
In industry, the cost of production is an important factor and it is preferred to use conventional and low cost procedures for producing the parts. Heat treatment cycles and alloying additions are the key factors affecting the microstructure and mechanical properties of the cast steels. In this study an attempt was made to evaluate the influence of minor Mo addition on the microstructure and me...
متن کاملThe Influence of Homogenization and Solution Annealing Process on the Microstructure and Mechanical Properties of 1.4470 Ferritic-austenitic Stainless Steel
In the present research, the effect of the homogenization process and annealing temperature were investigated for the 1.4470 ferritic-austenitic stainless steel in the as-cast condition. In this regard, microstructural evolutions, hardness, and impact energy of the steel was evaluated with different heat treatment conditions. The results show that the minimum volume fraction of austenite phase ...
متن کاملEVALUATION OF THE MECHANICAL PROPERTIES OF NIOBIUM MODIFIED CAST AISI H 13 HOT WORK TOOL STEEL
Abstract: mechanical properties of AISIH 13 hot-work tool steel have been studied. Cast samples made of the modified new steel were homogenized and austenitized at different conditions, followed by tempering at the specified temperature ranges. Hardness, red hardness, three point bending test and Charpy impact test were carried out to evaluate the mechanical properties together with characteriz...
متن کامل