Magnetomechanical damping by polycrystalline TbDy
نویسندگان
چکیده
Vibration damping in polycrystalline TbDy alloys was studied at cryogenic temperatures. Mechanical hysteretic losses were measured at various strains, frequencies, and loading configurations at 77 K. Some textured TbDy materials demonstrated 22.6% energy dissipation in mechanical measurements at low frequency ~0.01 Hz! and a mean logarithmic decrement of 0.23 at a higher frequency ~25 kHz!. Ultrasonic velocities of longitudinal and shear elastic waves were measured on single and polycrystalline TbDy; little variation in ultrasonic velocities was found even for samples with large variation in crystallographic texture and magnetomechanical properties. © 2002 American Institute of Physics. @DOI: 10.1063/1.1452217#
منابع مشابه
Magnetomechanical effects in textured polycrystalline Tb76Dy24
Uniaxial stress-strain measurements were performed on polycrystalline Tb76Dy24 alloys which exhibit ‘‘giant magnetostriction’’ at cryogenic temperatures. The Young’s moduli were reduced by up to a factor of five at 77 K, in comparison to their values at 300 K. We attribute this reduction to a mechanical compliance from domain rotation. Large mechanical hysteresis is also found in nominally elas...
متن کاملHigh Damping Capacity Coatings for Surface Vibration Control
The damping capacity Q-'of a number of Fe-16%Cr alloys containing (0 6)%A1 and (0 4)%Mo has been investigated and compared to that of thermally sprayed coatings. The magnetomechanical hysteresis loss was determined using a cantilever method and based on the modal analysis technique of flat beam samples. Heat treatments usually enhanced the loss capability, but further annealing destroyed it dra...
متن کاملDetermination of the Gyromagnetic Ratio and the Magnetic Resonance Damping Coefficient of Ferrites
Resonance experiments are described on polycrystalline ferrite spheres in a microwave cavity with a linearly polarized magnetic field. Fundamental quantities, like the g-factor and the damping coefficient 'of the ferrite, are derived from the measurements. The damping coefficient can be calculated either from a linewidth measurement or from the maximum amount of absorption in the ferrite at res...
متن کاملIntrinsic and non-local Gilbert damping in polycrystalline nickel studied by Ti:Sapphire laser fs spectroscopy
The use of femtosecond laser pulses generated by a Ti:Sapphire laser system allows us to gain an insight into the magnetization dynamics on time scales from sub-picosecond up to 1 ns directly in the time domain. This experimental technique is used to excite a polycrystalline nickel (Ni) film optically and probe the dynamics afterwards. Different spin wave modes (the Kittel mode, perpendicular s...
متن کامل