One-dimensional single-crystalline Mn3O4 nanostructures with tunable length and magnetic properties of Mn3O4 nanowires.
نویسندگان
چکیده
A facile, solution-phase route to mass fabrication of one-dimensional single crystalline Mn(3)O(4) nanowires with a unique core/sheath heteronanostructure, controlled aspect ratios, and narrow diameter distribution was reported. The single crystalline Mn(3)O(4) nanowires have considerably large coercivities (H(C) > 1 T) at low temperatures.
منابع مشابه
Synthesis and characterization of nanowires Hausmannite (Mn3O4) by solid-state thermal decomposition
In this study, we synthesis one-dimensional (1D) manganese(III) Schiff base coordination polymer [Mn(Brsalophen)(μ1,3-N3)]n by reaction of MnCl2·6H2O and tetradentate Schiff base ligand Brsalophen at the presence of NaN3 in methanol and characterized by elemental analyses (CHN) and FT-IR spectroscopy. It was used as a new precurs...
متن کاملSynthesis and characterization of nanowires Hausmannite (Mn3O4) by solid-state thermal decomposition
In this study, we synthesis one-dimensional (1D) manganese(III) Schiff base coordination polymer [Mn(Brsalophen)(μ1,3-N3)]n by reaction of MnCl2·6H2O and tetradentate Schiff base ligand Brsalophen at the presence of NaN3 in methanol and characterized by elemental analyses (CHN) and FT-IR spectroscopy. It was used as a new precurs...
متن کاملBi-directional-bi-dimensionality alignment of self-supporting Mn3O4 nanorod and nanotube arrays with different bacteriostasis and magnetism.
Self-supported Mn3O4 patterns of aligned nanorods and nanotubes were synthesized through a bi-directional-bi-dimensionality growth model by using sodium gluconate and urea as additives under mild hydrothermal conditions without the use of any substrates. In one direction, Mn3O4 grows to form one-dimensional nanorods or nanotubes, while in the other direction Mn3O4 grows into two-dimensional nan...
متن کاملEngineering single crystalline Mn3O4 nano-octahedra with exposed highly active {011} facets for high performance lithium ion batteries.
Well shaped single crystalline Mn3O4 nano-octahedra with exposed highly active {011} facets at different particle sizes have been synthesized and used as anode materials for lithium ion batteries. The electrochemical results show that the smallest sized Mn3O4 nano-octahedra show the best cycling performance with a high initial charge capacity of 907 mA h g(-1) and a 50th charge capacity of 500 ...
متن کاملMagnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 47 4 شماره
صفحات -
تاریخ انتشار 2011