Water Absorption Behavior of Hemp Hurds Composites

نویسندگان

  • Nadezda Stevulova
  • Julia Cigasova
  • Pavol Purcz
  • Ivana Schwarzova
  • Frantisek Kacik
  • Anton Geffert
چکیده

In this paper, water sorption behavior of 28 days hardened composites based on hemp hurds and inorganic binder was studied. Two kinds of absorption tests on dried cube specimens in deionized water bath at laboratory temperature were performed. Short-term (after one hour water immersion) and long-term (up to 180 days) water absorption tests were carried out to study their durability. Short-term water sorption behavior of original hemp hurds composites depends on mean particle length of hemp and on binder nature. The comparative study of long-term water sorption behavior of composites reinforced with original and chemically modified hemp hurds in three reagents confirmed that surface treatment of filler influences sorption process. Based on evaluation of sorption curves using a model for composites based on natural fibers, diffusion of water molecules in composite reinforced with original and chemically modified hemp hurds is anomalous in terms of the Fickian behavior. The most significant decrease in hydrophility of hemp hurds was found in case of hemp hurds modified by NaOH and it relates to change in the chemical composition of hemp hurds, especially to a decrease in average degree of cellulose polymerization as well as hemicellulose content. OPEN ACCESS Materials 2015, 8 2244

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Changes in the Properties of Composites Caused by Chemical Treatment of Hemp Hurds

The possibility of using industrial hemp as a source of natural fibers for purpose of construction, mainly for the preparation of lightweight composites based on hemp hurds is described. In this article, an overview of measurement results of important technical parameters (compressive strength, density, thermal conductivity) of composites based on organic filler chemically modified hemp hurds i...

متن کامل

Complete Chemical Analysis of Carmagnola Hemp Hurds and Structural Features of Its Components

As interest in lignocellulosic biomass as a feedstock for conversion into biofuels is steadily growing, analysis of its components becomes ever more important. The complete chemical composition of waste hemp hurds from the industrial variety “Carmagnola” has been determined to optimize its utilization as a raw material. The results from chemical analysis show that hemp hurds contain 44.0% alpha...

متن کامل

Mechanical Properties and Water Absorption of Hemp Fibers–Reinforced Unsaturated Polyester Composites: Effect of Fiber Surface Treatment with a Heterofunctional Monomer

Hemp fibers–reinforced unsaturated polyester (UP) composites were prepared by hand lay-out compression molding. Hemp fibers were treated with isocyanatoethyl methacrylate (IEM), using dibutyltin dilaurate as a catalyst. The results indicated that fiber treatment significantly increased tensile strength, flexural strength, flexural modulus, and water resistance of the resulting composites, and y...

متن کامل

Properties Characterization of Chemically Modified Hemp Hurds

The effect of chemical treatment of hemp hurds slices in three solutions (EDTA (Ethylenediaminetetraacetic acid), NaOH and Ca(OH)₂) on the properties of natural material was discussed in this paper. Changes in the morphology, chemical composition and structure as well as thermal stability of hemp hurds before and after their modification were investigated by using FTIR (Fourier transform infrar...

متن کامل

Effect of water absorption on the mechanical properties of hemp fibre reinforced unsaturated polyester composites

Hemp fibre reinforced unsaturated polyester composites (HFRUPE) were subjected to water immersion tests in order to study the effects of water absorption on the mechanical properties. HFRUPE composites specimens containing 0, 0.10, 0.15, 0.21 and 0.26 fibre volume fraction were prepared. Water absorption tests were conducted by immersing specimens in a de-ionised water bath at 25 C and 100 C fo...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 8  شماره 

صفحات  -

تاریخ انتشار 2015