Reciprocating sliding friction and wear behavior of electrical discharge machined zirconia-based composites against WC–Co cemented carbide
نویسندگان
چکیده
a Department of Mechanical Construction and Production, Ghent University (UGent), IR04, Sint-Pietersnieuwstraat 41, B-9000 Gent, Belgium b Department of Metallurgy and Materials Engineering, Catholic University Leuven (K.U. Leuven), MTM, Kasteelpark Arenberg 44 (bus 2450), B-3001 Leuven, Belgium c Department of Mechanical Engineering, Catholic University Leuven (K.U. Leuven), PMA, Celestijnenlaan 300 B (bus 2420), B-3001 Leuven, Belgium
منابع مشابه
Influence of electrical discharge machining on sliding friction and wear of WC–Ni cemented carbide
Tribological characteristics of fine-grained WC–8 wt%Ni with different surface finishing conditions corresponding to sequential wire electrical discharge machining (wire-EDM) or grinding were investigated by performing dry reciprocating sliding experiments on TE77 pin-on-plate equipment with WC–6 wt%Co as mating material. Surface finishes and wear surfaces were characterized using surface topog...
متن کاملEDM machinability and dry sliding friction of WC-Co cemented carbides
A number of WC-Co cemented carbides with 6–12 wt. % Co were machined and surface finished by grinding or Electrical Discharge Machining (EDM). EDM was executed in deionised water through several consecutive gradually finer steps. Correlations between Material Removal Rate (MRR), surface finish and EDM parameters were derived. The quality and integrity of surface finishes were analysed by Scanni...
متن کاملWear Behavior in Micro and Nano-Structured WC-9Co-0.7VC Cemented Carbide Produced by Rapid Hot Press Sintering
The effect of CaO on the formation of β- and γ-zirconia nanoparticles from α-zirconia was investigated and their stability evaluated via mechanical activation. α-ZrO2+8.5wt%CaO powder was milled for 2-150 hours with ball-to-powder weight ratios (BPWR) of 40:1 and 60:1. Structural evaluations were conducted using X-Ray diffraction and scanning electron microscope (SEM). Thermal analysis wa...
متن کاملEffect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملEffect of SiC nanoparticles addition on mechanical properties and wear resistance of cemented carbides fabricated by spark plasma sintering
WC-10Co cemented carbides containing 1 to 4 wt% SiC nanoparticles were prepared by spark plasma sintering. The effects of SiC content on microstructure, mechanical properties and wear resistance of the sintered materials were studied. Microstructural studies showed that SiC addition resulted in WC grain coarsening. In addition, the hardness decreased with increasing SiC content. However, the fr...