Effect of reaction conditions on size and morphology of ultrasonically prepared Ni(OH)(2) powders.
نویسندگان
چکیده
Modern electrochemical devices require the morphological control of the active material. In this paper the synthesis of nickel hydroxide, as common active compound of such devices, is presented. The influence of ultrasound in the synthesis of nickel hydroxide from aqueous ammonia complexes is studied showing that ultrasound allows the fabrication of flower-like particles with sizes ranging in between 0.7 and 1.0μm in contrast with the 6-8μm particles obtained in the absence of ultrasound. The influence of gas flow, temperature of the process and surfactants in the ultrasonically prepared powders is discussed in term of shape, size and agglomeration of the particles. Adjusting the experimental condition, spherical or platelet-like particles are obtained with sizes ranging from 1.3μm to 200nm.
منابع مشابه
Effect of Ni content on the reaction behaviors and microstructure of TiB2-TiC/Ni cermets synthesized by MASHS
In this paper TiB2-TiC/Ni cermet with various Ni (20, 40 and 60 wt %) content were synthesized by mechanically activated self-propagating synthesis (MASHS) and effect of the addition of Ni on synthesis parameters and microstructure of synthesized samples were investigated. First raw materials (B4C, Ti and Ni) milled in Ar atmosphere. Then milling powders analyzed by XRD. In next step powders sy...
متن کاملEffect of calcination process on the gas phase photodegradation by CuO-Cu2O/TiO2 nanocomposite photocatalyst
A series of CuO-Cu2O/TiO2 nanocomposite samples were prepared by the sol-gel method. Before applying the sol-gel method, the Cu(OH)2 nanostructure on Cu powders were formed by in-situ solution treatment. The samples were characterized through some techniques and the photocatalytic performance of CuO-Cu2O/TiO2 nanocomposites for gas-phase 2-propanol photo-oxidation under UV and sunlight type ill...
متن کاملTHE EFFECT OF RAW MATERIALS CONCENTRATION ON HYDROXYAPATITE POWDER CHARACTERISTICS AND SINTERING BEHAVLOR
Ultrafine hydroxyapatite (HAp) powders with crystallite size in the range of 10-90 nm were synthesized by chemical precipitation process using Ca(OH)2 and H3PO4 solutions as starting materials. Molar ratio of Ca/P=1.68 was kept constant throughout the process and alkaline condition for the reaction was maintained using ammonium hydroxide. The role of raw material concentration on HAp crystallit...
متن کاملAnionic and Cationic Surfactants in Ammonia Gas-Mediated Synthesis of β-Ni(OH)2 and NiO Nanostructures
Up to now, researchers have proposed several synthesis methods for the preparation of β-nickel(II) hydroxide nanostructures. Most of these approaches contain harsh synthetic conditions such as multi-step processes, high temperatures and long reaction time. In this work, a novel, facile and low cost method is introduced to produce of β-Ni(OH)2 nanostructures using the gas-solution precipitation ...
متن کاملEffect of Surfactant in Formation of Hydroxyapatite Nano-Rods under Hydrothermal Conditions
Hydroxyapatite (HA) nano-rods with uniform morphology and controllable size have been successfully synthesized in the presence of cationic and non-ionic surfactants by a hydrothermal method. (NH4) 2HPO4 and Ca(NO 3)2.4H2O were used as the phosphorus and calcium sources, respectively. The composition of synthesized powders w...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Ultrasonics sonochemistry
دوره 18 4 شماره
صفحات -
تاریخ انتشار 2011