Secondary aluminium-iron (III) chloride batteries with a low temperature molten salt electrolyte
ثبت نشده
چکیده
Secondary aluminium-iron (III) chloride batteries using a low temperature molten salt electrolyte were constructed and tested. Discharge current densities were in the range 5 to 100mA ( ~ 1 to 2 0 m A c m 2 ; ~ C/4 to 5C); charging currents were 5 m A (C/4 toC/2). Utilization of the positive electrode reactant was low due to the discharge rates and loading procedure. The mode for self discharge was dissolution of the positive electrode reactant and transport to the aluminium negative electrode where it reacted.
منابع مشابه
Surface Morphology and Microstructure of Zinc Deposit From Imidazole with Zinc Chloride Low Temperature Molten Salt Electrolyte in The Presence of Aluminium Chloride
Low temperature molten salts have variety of applications in organic synthesis, catalytic processing, batteries and electrode position due to their air and water stability. They have wide potential window for their applications in voltage and temperature and hence there is a possibility to deposit metals which could not be deposited from aqueous electrolytes. Our aim and scope of our research w...
متن کاملElectrodeposition of Zinc From Low Temperature Molten Salt Electrolyte: Part I-Imidazole And Zinc-Chloride Electrolyte
Our R & D work was focused on the electro deposition of Zinc from imidazole as low temperature molten salt (LTMS) electrolyte with zinc chloride as a supporting salt at <100o C., without required controls from the previous existing non aqueous baths as well additive free system for the zinc deposition. Surface morphological studies and crystallographic orientation results were evaluated.
متن کاملMolten Triazolium Chloride Systems as New Aluminum Battery Electrolytes
The possibility of using molten mixtures of 1,4-dimethyl-l,2,4-triazolium chloride (DMTC) and aluminum chloride (A1C13) as secondary battery electrolytes was studied, in some cases extended by the copresence of sodium chloride. DMTC-A1CI~ mixtures demonstrated high specific conductivity in a wide temperature range. The equimolar system is most conductive and has K values between 4.02 x 10 -~ an...
متن کاملThe effects of different molten salt composition on morphology and purity of ZrB2 powder obtained via direct molten salt reaction method
Zirconium Diboride (ZrB2) powder was synthesized at low temperature via a Direct Molten Salt Reaction (DMSR) method. The influence of different salt compositions including eutectic mixture of (KF-NaF), (KF-KCl) and (KCl-NaCl) on the morphology and purity of the reaction products was studied. The obtained samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD...
متن کاملFacile molten salt synthesis of Li2NiTiO4 cathode material for Li-ion batteries
Well-crystallized Li2NiTiO4 nanoparticles are rapidly synthesized by a molten salt method using a mixture of NaCl and KCl salts. X-ray diffraction pattern and scanning electron microscopic image show that Li2NiTiO4 has a cubic rock salt structure with an average particle size of ca. 50 nm. Conductive carbon-coated Li2NiTiO4 is obtained by a facile ball milling method. As a novel 4 V positive ca...
متن کامل