3-D solar cells by electrochemical-deposited Se layer as extremely-thin absorber and hole conducting layer on nanocrystalline TiO2 electrode

نویسندگان

  • Duy-Cuong Nguyen
  • Souichirou Tanaka
  • Hitoshi Nishino
  • Kyohei Manabe
  • Seigo Ito
چکیده

A three-dimensional selenium solar cell with the structure of Au/Se/porous TiO2/compact TiO2/fluorine-doped tin oxide-coated glass plates was fabricated by an electrochemical deposition method of selenium, which can work for the extremely thin light absorber and the hole-conducting layer. The effect of experimental conditions, such as HCl and H2SeO3 in an electrochemical solution and TiO2 particle size of porous layers, was optimized. This kind of solar cell did not use any buffer layer between an n-type electrode (porous TiO2) and a p-type absorber layer (selenium). The crystallinity of the selenium after annealing at 200°C for 3 min in the air was significantly improved. The cells with a selenium layer deposited at concentrations of HCl = 11.5 mM and H2SeO3 = 20 mM showed the best performance, resulting in 1- to 2-nm thickness of the Se layer, short-circuit photocurrent density of 8.7 mA/cm2, open-circuit voltage of 0.65 V, fill factor of 0.53, and conversion efficiency of 3.0%.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Optimization of Annealing Process for Totally Printable High-current Superstrate CuInS2 Thin-Film Solar Cells

Planar superstrate CuInS2 (CIS) solar cell devices are fabricated using totally solution-processed deposition methods. A titanium dioxide blocking layer and an In2S3 buffer layer are deposited by the spray pyrolysis method. A CIS2 absorber layer is deposited by the spin coating method using CIS ink prepared by a 1-butylamine solvent-based solution at room temperature. To obtain optimum annealin...

متن کامل

Improving the optical properties of thin film plasmonic solar cells of InP absorber layer using nanowires

In this paper, a thin-film InP-based solar cell designed and simulated. The proposed InP solar cell has a periodic array of plasmonic back-reflector, which consists of a silver layer and two silver nanowires. The indium tin oxide (ITO) layer also utilized as an anti-reflection coating (ARC) layer on top. The design creates a light-trapping structure by using a plasmonic back-reflector and an an...

متن کامل

Investigation of Physical Properties of e-Beam Evaporated CdTe Thin Films for Photovoltaic Application

CdTe thin films with 2.8 µm thickness were deposited by electron beam evaporation method. X-ray diffraction, scanning electron microscopy, UV-Vis-NIR spectroscopy and atomic force microscopy (AFM) were used to characterize the films. The results of AFM analysis revealed that the CdTe films have uniform surface. CdTe thin films were heat-treated by SnCl2 solution. Structural analysis using XRD s...

متن کامل

Electron-Selective TiO2 Contact for Cu(In,Ga)Se2 Solar Cells

The non-toxic and wide bandgap material TiO2 is explored as an n-type buffer layer on p-type Cu(In,Ga)Se2 (CIGS) absorber layer for thin film solar cells. The amorphous TiO2 thin film deposited by atomic layer deposition process at low temperatures shows conformal coverage on the CIGS absorber layer. Solar cells from non-vacuum deposited CIGS absorbers with TiO2 buffer layer result in a high sh...

متن کامل

Fabrication of dye sensitized solar cells with a double layer photoanode

Dye sensitized solar cell was fabricated from a double layer photoanode. First, TiO2 nanoparticles  were synthesized by hydrothermal method. These TiO2 NPs were deposited on FTO glasses by electrophoretic deposition  method in applied voltage of 5 V and EPD time of 2.5-10 min. Then TiO2 hollow spheres (HSs) were synthesized by sacrificed template method with Carbon Spheres as template and TTIP ...