Reaction between MnO-SiO2-FeO Inclusion and Steel Matrix Deoxidized by Si and Mn at Different Heat Treatment Temperatures
نویسندگان
چکیده
In order to clarify the effect of heat-treatment temperature on the reaction between solid steel and inclusions, in this study, the reaction between Fe-Mn-Si alloy and MnO-SiO2-FeO oxide during heat-treatment at 1373 K, 1473 K and 1573 K were investigated using diffusion couple method, respectively. The results indicate that the width of the particle-precipitated zone (PPZ) and the Mndepleted zone (MDZ) increased with increasing heat-treatment temperature from 1373 K to 1473 K. However, compared with the experimental results at 1473 K, the precipitated particles in the alloy were significantly coarsened and the width of the PPZ decreased at 1573 K. In addition, with increasing heat-treatment time at 1573 K, the composition of the oxide changed from 2MnO·SiO2 to MnO·SiO2 and the manganese and silicon in the oxide obviously diffused into the alloy, resulting in a significant increase of Mn and Si contents in the alloy near the interface.
منابع مشابه
Comparative study on the effect of heat treatment temperatures on colorimetric properties of CoFe2O4 nanoparticles and CoFe2O4/SiO2 nanocomposites
In this paper, a comparative study on the effect of different heat treatment temperatures, i.e., 400, 500, 600 and 700 oC on colorimetric properties of CoFe2O4 nanoparticles has been done for the first time. Then, the mentioned Co-Fe mixed oxide pigments are dispersed in an amorphous silicon oxide matrix to form CoFe2O4/SiO2 nanocomposites. In the next step, the optical properties of nanocompos...
متن کاملThe Effect of Two-stage Heat Treatment Temperatures on Initial and FSSWed Properties of TRIP Steels
In this paper, a 0.2 C–1.6 Mn–1.5 Si wt. % TRIP-aided cold-rolled steel sheet was fabricated and the optimal heat treatment conditions (Intercritical Annealing “IA” and Bainitic Isothermal Transformation “BIT”) were investigated to maximize the volume fraction and stability of the retained austenite. The effects of temperature on IA (770, 790 and 810 ºC) and BIT (330, 350 and 370 <su...
متن کاملAn Investigation of Casting Defects Revealed in Forming Process of USD7 Steel
USD7 is one of the steel products of Isfahan Steel Company. It is cast in continuous casting moulds and rolled up to a rod of 5 mm diameter. Finally, it is wire drawn up to 3 mm and used as welding electrodes. This steel contains 0.05 to 0.09 wt. % carbon. The acceptable limit of the aluminium in this class of steel is less than 0.003 wt%. Therefore, it is categorized as rimmed steel...
متن کاملEFFECT OF COMPOSITION ON PHASE EVOLUTION AND MICROSTRUCTURE OF REACTION BONDED MULLITE (RBM)
Compositions of Al2O3+Si, SiO2+Al and Al+Si systems were prepared to study the effect of reaction bonding process on the mullite formation. The composition of each system was adopted according to mullite stoichiometery and sintered in 700-1600°C range. Results showed that the formation of reaction bonded mullite starting from Al2O3+Si mixtures, proceeded in two partially overlapping steps, the ...
متن کاملImpacts of Modification of Alloying Method on Inclusion Evolution in RH Refining of Silicon Steel
This study explores the effect of introducing additional alloy elements not only in a different order but also at different stages of the Ruhrstahl-Heraeus (RH) process of low-carbon silicon steel production. A more economical method, described as "pre-alloying", has been introduced. The evolution of MnO-FeO inclusions produced by pre-alloying was investigated. Results show that spherical 3FeO·...
متن کامل