Electron microscopy characterization of hot - pressed Al substituted
نویسنده
چکیده
Hot-pressing was used to prepare a dense (97% relative density) cubic Al substituted Li7La3Zr2O12 material at temperatures lower than typically used for solid-state and/or liquid phase sintering. Electron microscopy analysis revealed equiaxed grains, grain boundaries, and triple junctions free of amorphous and second phases and no Al segregation at grain boundaries. These results suggest that Al2O3 and/or Al cannot act as a sintering aid by reducing grain boundary mobility. If Al2O3 acts as a sintering aid its main function is to enter the lattice as Al to increase the point defect concentration of the slowest moving species. REPORT DOCUMENTATION PAGE (SF298) (Continuation Sheet) Continuation for Block 13
منابع مشابه
Mechanical properties of hot-pressed Al-4.5 wt. % Cu/WC composite
In this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an Al-4.5 wt% Cu powder alloy. The WC nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the WC nanoparticles on the mechanical properties of the fabricated composite p...
متن کاملAn Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500...
متن کاملAn Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500...
متن کاملA Study of the Nanostructure and Hardness of Electron Beam Evaporated TiAlBN Coatings
TiAlBN coatings have been deposited by electron beam (EB) evaporation from a single TiAlBN material source onto AISI 316 stainless steel substrates at a temperature of 450C and substrate bias of -100 V. The stoichiometry and nanostructure have been studied by x-ray photoelectron spectroscopy, x-ray diffraction and transmission electron microscopy. The hardness and elastic modulus were determin...
متن کاملبررسی اثر حضور آلومینیوم اضافی در مخلوط پودری TiO2-Al و نوع ماده جاذب در ساخت ریزموجی کامپوزیت TiAl/Al2O3
In this research, TiAl/Al2O3 composite was synthesized from mechanically activated TiO2-Al powder mixtures using microwave heating.The initial powder mixtures were mechanically activated and pressed into cylindrical tablets and then heated in a microwave oven. The effect of different amounts of excess Al and microwave susceptor material (SiC or graphite) on the ignition time and the result...