Spectroscopic studies on Mn 2 + ions doped Cadmium Aluminum Fluoro Lead Borate Glass
نویسنده
چکیده
This article reports on optical properties of Mn 2+ (0.5 mol%): 49.5 B2O3 10PbO 30CdO -10AlF3 glasses. Optical absorption spectrum of the manganese ions doped glass exhibits broad absorption band at 473 nm. Photoluminescence spectrum of Mn 2+ (0.5 mol %): 49.5B2O330CdO – 10PbO 10AlF3 glass has revealed a red emission at 618 nm with an excitation wavelength 467 nm.
منابع مشابه
Near-infrared luminescence of rare earth ions in oxyfluoride lead borate glasses and transparent glass-ceramic materials
Oxyfluoride lead borate glasses singly doped with Nd3+ and Er3+ ions have been studied before and after thermal treatment. The orthorhombic PbF2 crystallites are formed during thermal treatment, which was evidenced by X-ray diffraction analysis. Near-infrared luminescence spectra at 1.06 μm and 1.53 μm have been registered for samples before and after annealing, which correspond to the main F3/...
متن کاملCombined DFT, Deconvolution Analysis for Structural Investigation of Copper –doped Lead Borate Glasses
Samples from binary lead borate glass system doped with minor quantities of copper have been prepared by conventional melt-annealing technique. X-ray diffraction (XRD) has been used to prove the amorphous nature of prepared glasses. Structural and optical properties were investigated using FTIR and UV-vis. Spectroscopic investigations were approved using density function theory (DFT) calculatio...
متن کاملOptical and structural properties of lithium sodium borate glasses doped Dy3+ ions Abstract Absorption and emission spectra of lithium sodium borate glass doped with different concentrations
Absorption and emission spectra of lithium sodium borate glass doped with different concentrations of Dy3+ have been reported. The concentration of Dy3+ was varied from 0.3 to 1.3 mol%. The amorphous nature of the prepared samples was confirmed by the X-ray Diffraction (XRD). Fourier transforms infrared (FTIR) spectra, and other significant physical properties (energy band gap, density, ion con...
متن کاملMicrowave Absorption of Barium Borosilicate, Zinc Borate, Fe-Doped Alumino-Phosphate Glasses and Its Raw Materials
This study presents microwave absorption of raw materials used in barium borosilicate, Fe-doped alumina phosphate and zinc borate glass. Microwave absorption was investigated for the raw materials SiO2, Na2CO3, BaCO3, BPO4, Al(PO3)3, Mg(PO3)2, Al(OH)3, TiO2. The study shows that SiO2 could be heated directly above 1000 °C within 30 min at 1.5 kW microwave output (MW) power and 0.8 kW MW power i...
متن کاملSpectroscopic properties and energy transfer parameters of Er3+- doped fluorozirconate and oxyfluoroaluminate glasses
Er3+-doped fluorozirconate (ZrF4-BaF2-YF3-AlF3) and oxyfluoroaluminate glasses are successfully prepared here. These glasses exhibit significant superiority compared with traditional fluorozirconate glass (ZrF4-BaF2-LaF3-AlF3-NaF) because of their higher temperature of glass transition and better resistance to water corrosion. Judd-Ofelt (J-O) intensity parameters are evaluated and used to comp...
متن کامل