Fibers from Soybean Protein and Poly(vinyl alcohol)
نویسندگان
چکیده
Bicomponent fibers were wet-spun from soybean protein and poly(vinyl alcohol). The protein core of the spun bicomponent fiber was brittle and showed a high frequency of core breakage upon drawing. Our effort was then to study the soybean protein solution, with the aim of trying to understand the cause for fiber brittleness and to determine the optimum solution conditions for fiber spinning. The effects of alkali, urea, and sodium sulfite on the viscosity of the soybean protein solution were examined. The hydrolytic stability of the soybean protein solution was examined at various pH values at two temperatures (room temperature and 60°C). Both the viscosity and gel electrophoresis were used for this purpose. The degradation of the soybean protein and the existing microgels in the protein spinning solution were thought to be the causes for the poor fiber drawability. Extent of protein denaturation will also effect the fiber drawability. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 11–19, 1999
منابع مشابه
Chitosan/nanosilver Nanofiber Composites with Enhanced Morphology and Microbiological Properties
In recent years natural polymers have been widely used in biomedical applications. Application of natural and biocompatible polymers in wound dressing, medical sutures and tissue engineering are extensively growing. Additional properties are provided when metal nanoparticles such as silver and gold are incorporated in to the fibers. However, nowadays nanofibers due to their inherent properties ...
متن کاملFabrication of Polyvinyl Alcohol/Kefiran Nanofibers Membrane Using Electrospinning
The Poly (vinyl alcohol)/Kefirane nanofiber membrane was successfully fabricated for the firsttime using electrospinning of the polyvinyl alcohol (PVA) and Kefirane blend solution. Scanningelectron microscope (SEM), attenuated total reflectance Fourier transform infrared (ATRFT-IR), and differential scanning calorimetry (DSC) were used to characterize the electrospunPoly (vinyl alcohol)/Kefiran...
متن کاملSynthesis of pH Sensitive Hydrogels Based on Poly Vinyl Alcohol and Poly Acrylic Acid
In this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. Afterward, effects of time and heating on water uptake were investigated. The highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºC was about 2129% after 4 days at equilibrium state. Hydrogels exhibited p...
متن کاملBiological Properties of Blend Nanofibrous Scaffolds from Poly(caprolactone)-Chitosan-Poly(vinyl alcohol)
متن کامل
Preparation and Characterization of Aligned and Random Nanofibrous Nanocomposite Scaffolds of Poly (Vinyl Alcohol), Poly (e-Caprolactone) and Nanohydroxyapatite
Nanofibrous scaffolds produced by electrospinning have attracted much attention, recently. Aligned and random nanofibrous scaffolds of poly (vinyl alcohol) (PVA), poly (ε-caprolactone) (PCL) and nanohydroxyapatite (nHA) were fabricated by electrospinning method in this study. The composite nanofibrous scaffolds were subjected to detailed analysis. Morphological investigations revealed that the...
متن کامل